Chromatic baking-free tile and method for making same

A color and tile blank technology, which is applied in the production field of the color unfired tile, can solve the problems of waste of pigments and brighteners, etc., and achieve the effect of reducing consumption and production cost

Inactive Publication Date: 2008-09-03
孙士悦 +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this production method, all the materials are mixed together and pressed by pouring the mixed materials into the mold. However, since the pigment and brightener only need to work on the surface of the colored unburned tile, the existing There is a huge waste of pigments and brighteners in the production method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The colored non-burning tile and its production method are as follows:

[0017] The composition ratio of the lower layer material is calculated by weight: cement 100, sand 150, water 25.

[0018] The composition ratio of the upper layer material is calculated by weight: cement 100, water 60, iron oxide red 10, brightener 5.

[0019] The ratio of the lower material to the upper material is by weight: 18 for the lower layer and 1 for the upper layer.

[0020] (1) mix the material that forms the lower layer and the material that forms the upper layer respectively, and set aside for use;

[0021] (2) moulding the mixture of the lower layer material and compacting to obtain a tile blank;

[0022] (3) the mixture of the upper layer material is evenly coated on the surface of the tile;

[0023] (4) Demoulding and maintenance of tile blanks.

Embodiment 2

[0025] The colored non-burning tile and its production method are as follows:

[0026] The composition ratio of the lower material is calculated by weight: cement 100, sand 130, water 30.

[0027] The composition ratio of the upper layer material is calculated by weight: cement 100, water 50, chromium oxide green 8, brightener 4.

[0028] The ratio of the lower layer material to the upper layer material is by weight: 20 for the lower layer and 1 for the upper layer.

[0029] (1) mix the material that forms the lower layer and the material that forms the upper layer respectively, and set aside for use;

[0030] (2) moulding the mixture of the lower layer material and compacting to obtain a tile blank;

[0031] (3) the mixture of the upper layer material is evenly coated on the surface of the tile;

[0032] (4) Demoulding and maintenance of tile blanks.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A color burn-free tile and method for the production thereof relates to the field of building material technology, in particular to a color burn-free tile and method for the production thereof. The color burn-free tile comprises cement, sand, water, paint and brightener and is characterized in two-layered structure, wherein the lower layer consists of cement, sand and water and the upper layer consists of cement, water, paint and brightener. The method of producing color burn-free tiles includes: evenly mixing the upper and the lower layers; producing the lower deck into a tile billet; evenly coating the upper layer on the surface of the tile billet; stripping, conserving and obtaining the product. Compared with the prior art, the color burn-free tile greatly reduces the consumption of two raw materials byusing paint and brightener only in the upper layer and greatly reduces the production cost while maintaining the effect of the prior products in the market.

Description

technical field [0001] The present invention relates to the technical field of building materials, in particular, to a colored non-burning tile, and also to a manufacturing method of the colored non-burning tile. Background technique [0002] In recent years, colored non-burning tiles have been more and more widely used because of their high quality and low price, and at the same time in line with the national policy of saving cultivated land. For example: Patent No. 02116465.7 "A colored glass unburned tile and its preparation method", the invention uses cement, sand, inorganic pigments and a mixture composed of polyvinyl alcohol and melamine formaldehyde resin. , demoulding and curing to get the finished product. In this production method, all the materials are mixed together, and the mixed materials are poured into the mold to be pressed, but since the pigment and brightener only need to work on the surface of the colored non-burning tile, the existing There is a huge w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00B28B3/00C04B41/61C04B14/06
Inventor 赵大洲孙士悦赵银平
Owner 孙士悦