Method for producing titanium tetrachloride using low grade titan raw material

A low-grade titanium and titanium tetrachloride technology, applied in the direction of titanium tetrachloride and titanium halide, can solve the problems that large-scale continuous industrial production cannot be realized, and achieve the effect of saving costs

Active Publication Date: 2009-01-07
PANZHIHUA IRON AND STEEL +2
View PDF1 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Chinese patent 200610021468.4 "Method for Extracting Iron Titanium Vanadium from High-Titanium Ferrovanadium Concentrate" mentioned the chlorination process of vanadium-titanium-chromium slag, but the raw material for this process is high-titanium ferrovanadium concentrate, and the The process cannot realize large-scale continuous industrial production
There is no relevant technical report on the production of titanium tetrachloride by chlorination of low-grade titanium ore abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing titanium tetrachloride using low grade titan raw material
  • Method for producing titanium tetrachloride using low grade titan raw material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment one uses the inventive method to prepare titanium tetrachloride

[0033] Blast furnace slag carbide slag and chlorine gas are used as reaction raw materials, and the diameter of the furnace body is 200mm.

[0034] Add 20kg of fresh carbonized slag and chlorination residue into the chlorination furnace in a ratio of 1:1, heat the charge, and when the temperature of the charge rises to 400°C, start to feed chlorine and air in a ratio of 75%, that is, the amount of chlorine feed is 6m 3 / h, dry air feed rate is 2m 3 / h, the feeding rate of fresh material is 30kg / h, and the amount of residue returning to the furnace is 10kg / h. The solid material residence time is 40min, the temperature is controlled at 640°C±10°C, the system runs stably for more than 8h, the chlorination rate of titanium carbide in the raw material is 91%, and 76kg of crude titanium tetrachloride is collected through the condensation system.

Embodiment 2

[0035] Embodiment two uses the inventive method to prepare titanium tetrachloride

[0036] Blast furnace slag carbide slag and chlorine gas are used as reaction raw materials, and the diameter of the furnace body is 200mm.

[0037] Add 20kg of fresh carbonized slag and chlorination residue into the chlorination furnace in a ratio of 1:1, heat the charge, and when the temperature of the charge rises to 400°C, start to feed chlorine and air in a 50% ratio, that is, the amount of chlorine gas feed is 4m 3 / h, dry air feed rate is 4m 3 / h, the feeding rate of fresh material is 25kg / h, and the amount of residue returning to the furnace is 15kg / h. The solid material residence time is 28min, the temperature is controlled at 610°C±10°C, the system runs stably for more than 8h, the chlorination rate of titanium carbide in the raw material is 86%, and 63kg of crude titanium tetrachloride is collected through the condensation system.

Embodiment 3

[0038] Embodiment three uses the inventive method to prepare titanium tetrachloride

[0039] Blast furnace slag carbide slag and chlorine gas are used as reaction raw materials, and the diameter of the furnace body is 200mm.

[0040] Add 20kg of fresh carbonized slag and chlorination residue into the chlorination furnace at a ratio of 1:1, heat the charge, and when the temperature of the charge rises to 400°C, feed pure chlorine gas with a flow rate of 6m 3 / h, the feeding rate of fresh material is 35kg / h, and the amount of residue returning to the furnace is 5kg / h. The solid material residence time is 42min, the temperature is controlled at 610°C±10°C, the system runs stably for more than 8h, the chlorination rate of titanium carbide in the raw material is 84%, and 88kg of crude titanium tetrachloride is collected through the condensation system.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for producing titanium tetrachloride by using a low grade titanium material, and belongs to the chemical technical field. The technical problem to be solved is to provide a method for producing titanium tetrachloride by using the low grade titanium material in continuous industrialized production. The method is characterized in that the low grade titanium material containing a certain proportion of titanium carbide is adopted to directly react with chlorine at the temperature of 600 DEG C to 700 DEG C to produce titanium tetrachloride. Long period continuous stable operation can be kept by using the technological parameters of the invention, and chlorination rate of titanium carbide in titanium material reaches above 90 percent, so that the titanium can be better used for producing titanium tetrachloride.

Description

technical field [0001] The invention belongs to the field of chemical industry and relates to a process for producing titanium tetrachloride by boiling chlorination, in particular to a method for producing titanium tetrachloride by using low-grade titanium raw materials. Background technique [0002] With the rapid development of the world's titanium industry, titanium ore resources have become one of the important factors restricting the titanium industry. Since high-grade titanium ore resources were exploited in large quantities in the early stages of the development of the titanium industry, currently there are fewer and fewer high-grade titanium ore resources, and the production areas are also very concentrated, monopolized by a few large groups, while low-grade titanium ore resources are widely distributed. , exist in various forms and have large reserves, so the development of boiling chlorination process for low-grade titanium raw materials can not only solve the curr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01G23/02
CPCC01G23/022C01G23/024
Inventor 陆平杨仰军黄家旭陈祝春刘森林杨文
Owner PANZHIHUA IRON AND STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap