Repairing agent for cement concrete bridge deck thin layer

A technology of cement concrete and repairing agent, which is applied in the field of repairing materials, and can solve problems such as shedding and cracking of pavement laminates, and achieve the effects of improving crush resistance, benefiting driving safety, and improving crack resistance

Inactive Publication Date: 2009-01-07
南京派尼尔科技实业有限公司
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] What the present invention aims to solve is the problem that the pavement laminates of cement concrete bridge decks are prone

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Repairing agent for cement concrete bridge deck thin layer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A component is selected from the pure acrylic emulsion of 5% cement weight;

[0047] B component is 16% of cement weight, and its proportioning is as follows:

[0048] Calcium sulfoaluminate concrete expansion agent 35%, Yuanming powder 20%, Naphthalene superplasticizer 6%, Synthetic crude fiber 2%, Class II fly ash 37%,

Embodiment 2

[0050] Component A is selected from pure acrylic emulsion with 10% cement weight;

[0051] The weight of component B cement is 16%, and its proportioning ratio is as follows:

[0052] Calcium sulphoaluminate concrete expansion agent 45%, Yuanming powder 5%, Naphthalene superplasticizer 6%, Synthetic crude fiber 6%, Class II fly ash 38%

Embodiment 3

[0054] Component A is selected from pure acrylic emulsion with 10% cement weight;

[0055] The weight of component B cement is 12%, and its proportion is as follows:

[0056] Calcium sulfoaluminate concrete expansion agent 75%, Yuanming powder 13%, Naphthalene superplasticizer 6%, Synthetic crude fiber 6%, Fly ash 0%

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a cement concrete deck lamina repairing agent, which comprises a component A and a component B. The component A is polymer emulsion which is either pure acrylic emulsion or styrene-acrylate emulsion. The component B is a powdered material rich in fiber, which is prepared with the following components by weight: 35 to 75 percent of an expansion agent; 0 to 20 percent of sodium sulphate; 0 to 6 percent of a water reducer; 0.5 to 6.0 percent of synthetic coarse fiber, 0 to 42 percent of pulverized fuel ash or powdered ore. After the component A and the component B are added to and mixed in concrete mixture pro rata, the repaired hardened concrete and the original concrete have high crack resistance, crush resistance, impact and grinding resistance and stripping resistance; the repaired concrete can be open to traffic after 24 hours. The cement concrete deck lamina repairing agent can be used for repairing laminae of cement concrete deck and road.

Description

【Technical field】 [0001] The invention relates to a patching material for a crack-resistant and peel-off-resistant thin layer of a cement concrete bridge deck. 【Background technique】 [0002] During the operation of the cement concrete bridge deck, the pavement laminates are prone to cracking and falling off. The damage of the bridge deck pavement is mainly caused by the following factors: [0003] 1. The rigidity of the bridge deck is insufficient, which causes large deformation under the action of heavy loads, coupled with the continuous impact and vibration of the vehicle, cracks appear on the bridge deck and pavement, and develop rapidly. [0004] 2. The bonding capacity between the pavement layer and the beam surface is insufficient. Under the load, the pavement layer and the main load-bearing member cannot work as a whole to bear the external load, which destroys the integrity of the concrete. Under the action of load, it is easy to cause peeling, cracking, peeling an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/02C04B22/14C04B16/06C04B18/08C04B111/72
CPCC04B26/06C04B2111/00482C04B2103/302C04B2111/0075C04B2111/72C04B40/0039Y02W30/91C04B24/2641C04B16/06C04B18/08C04B22/008C04B22/147C04B7/323C04B18/12C04B24/226C04B40/065
Inventor 叶德平朱瑾
Owner 南京派尼尔科技实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products