Transparent halogen-free fire-resisting paint constituent

A technology of fire-resistant coatings and compositions, applied in the direction of fire-resistant coatings, epoxy resin coatings, polyurea/polyurethane coatings, etc., can solve the problems of the base material of the coating part losing its original style, white opaque coating, black coating, etc., to achieve shortening coating Cloth processing time, shortening of hardening time, improvement of the effect of fire prevention mechanism

Inactive Publication Date: 2009-05-20
CHINA GENERAL PLASTICS
View PDF1 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For example, China Taiwan Patent Announcement 419514 is a foamed fireproof coating, in which polyphosphate amine is used as a carbonization accelerator, and the fireproofness is insufficient. In addition, expandable graphite is used to increase the strength and toughness of the coke expansion layer, but adding graphite will cause coating If it turns black, it will cause the base material of the coated part not only to lose its original style, but also to turn the surface black and unsightly
[0006] For example, China Taiwan patent announcement 499469 is based on water-based phosphorus-containing epoxy resin and melamine, supplemente

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent halogen-free fire-resisting paint constituent
  • Transparent halogen-free fire-resisting paint constituent

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example one

[0029] The formula is as shown in Table 3:

[0030] raw material name phr Remarks Polyurethane resin 100 Adhesive Methyl ethyl ketone 100 Solvent water 200 Solvent Melamine 100 Foaming agent Urea 100 Foaming agent Isoprene 120 Carbonizing agent Phosphorus titanate 60 Carbonization accelerator

Example Embodiment

[0031] Example two

[0032] The formula is as follows in Table 4:

[0033] raw material name phr Remarks Polyurethane resin 100 Adhesive Methyl ethyl ketone 100 Solvent water 200 Solvent Melamine 100 Foaming agent Urea 100 Foaming agent Isoprene 120 Carbonizing agent Phosphorus titanate 60 Carbonization accelerator Nano Mica 12 Auxiliary additives

[0034] Preparation method

[0035] The foaming agent and carbonizing agent of the above formula raw materials, if necessary, use auxiliary additives, and the solvent is fully mixed and dispersed at room temperature, then the carbonization accelerator is added and mixed, and finally the binder is added and mixed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a transparent halogen-free fire-retardant paint composition, which consists of 100phr (Parts per Hundred of Resin) of adhesive, 50-400phr of solvent, 50-300phr of foaming agent, 10-200phr of carburetant, 1-100phr of carbonizing promoter and 0-100phr of auxiliary additive; wherein, the carbonizing promoter is a phosphorus-containing compound with reaction functional groups. A coat formed by the transparent halogen-free fire-retardant paint composition nearly generates no smoke when being heated but instantly generates an expanding layer of high toughness. The expanding layer is not likely to crack, does not melt, drop and droop and moreover, is capable of effectively obstructing oxygen and heat to fulfill fire-retardant effect. The paint composition has excellent compatibility and dispersibility among the ingredients, therefore has eminent transparency and can be used for the fire prevention of various buildings, furniture or in decoration without damaging the original appearance view thereof.

Description

technical field [0001] The invention relates to a transparent halogen-free fireproof coating composition. The coating formed by the composition is almost smoke-free when heated, and can quickly form a high toughness, not easy to crack, not melt, and not drip. The expansion layer can effectively block oxygen and heat to achieve fireproof effect; and the compatibility between the components of the coating is very good, and the dispersion is good, forming superior transparency, which can be applied to various buildings, furniture or decorations It is fireproof and will not damage its original appearance. Background technique [0002] Due to the rapid growth of the global economy and the rapid development of the construction industry, the building materials or decoration materials used are mostly wood and polymer materials, but generally these materials are flammable. When a fire occurs, the flames spread rapidly. unstoppable. In recent years, people have gradually paid attent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/18C09D131/04C09D133/00C09D175/04C09D163/00C09D161/28
Inventor 吴协金李育奇林碧洲
Owner CHINA GENERAL PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products