Jewellery surface protective film and method for producing the same

A technology of surface protection film and production method, which is applied in the direction of jewelry, special surface, pretreatment surface, etc., can solve the problems of toxicity, easy wear, and easy damage of electroplated jewelry surface, and achieve the effect of preventing jewelry oxidation

Inactive Publication Date: 2009-07-15
陈远 +1
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the commonly used jewelry surface protection mostly uses a layer of metal plating on the jewelry surface, such as gold, silver, platinum, copper, rhodium, etc., to prevent the wear and loss of luster on the jewelry surface. Although these materials are easy to mold, shape, and polish, this This kind of electroplating surface is actually easy to wear and lose luster, and the surface of electroplated jewelry is easily damaged, which will also reduce the life and value of jewelry, and this coating method is not suitable for the surface of gemstones, especially fragile gemstones. In addition, the electroplating process will produce a large number of toxic pollutants, causing environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment 1, a kind of jewelry surface protective film, is made of the following raw materials in parts by weight: 3 parts of aminopropyltriethoxysilane, Al 2 o 3 1 part, SiO 2 25 parts, 25 parts of isopropanol, 35 parts of water, of which Al 2 o 3 , SiO 2 The particle size is 10nm.

[0025] The preparation method of above-mentioned jewelry surface protection film, comprises the following steps:

[0026] (1), in SiO 2 After first adding 12 parts (parts by weight) isopropanol in the micropowder and stirring evenly, add Al 2 o 3 Fine powder and aminopropyltriethoxysilane, and finally add the remaining isopropanol and water to mix and stir evenly to become the coating liquid for the protective film on the surface of jewelry;

[0027] (2) Remove dust and oil on the surface of jewelry, and keep the surface of jewelry clean, oil-free and dry;

[0028] (3) In a dust-free and oil-free environment, use a spray gun to spray the coating liquid of the jewelry protective f...

Embodiment 2

[0030] Embodiment 2, a kind of jewelry surface protective film, is made of the following raw materials in parts by weight: 1 part of aminopropyltriethoxysilane, Al 2 o 3 4 parts, SiO 2 20 parts, 30 parts of isopropanol, 42 parts of water, of which Al 2 o 3 , SiO 2 The particle size is 20nm.

[0031] The preparation method of above-mentioned jewelry surface protection film, comprises the following steps:

[0032] (1), in SiO 2 After first adding 15 parts (parts by weight) isopropanol in the micropowder and stirring evenly, add Al 2 o 3 Fine powder and aminopropyltriethoxysilane, and finally add the remaining isopropanol and water to mix and stir evenly to become the coating liquid for the protective film on the surface of jewelry;

[0033] (2) Remove dust and oil on the surface of jewelry, and keep the surface of jewelry clean, oil-free and dry;

[0034] (3) In a dust-free and oil-free environment, use a spray gun to spray the coating liquid of the jewelry protective f...

Embodiment 3

[0036] Embodiment 3, a kind of jewelry surface protection film is made of the following raw materials in parts by weight: 0.5 parts of aminopropyltriethoxysilane, Al 2 o 3 5 parts, SiO 2 15 parts, 20 parts of isopropanol, 40 parts of water, of which Al 2 o 3 , SiO 2 The particle size is 15nm.

[0037] The preparation method of above-mentioned jewelry surface protection film, comprises the following steps:

[0038] (1), in SiO 2 After first adding 10 parts (parts by weight) isopropanol in the micropowder and stirring evenly, then add Al 2 o 3 Fine powder and aminopropyltriethoxysilane, and finally add the remaining isopropanol and water to mix and stir evenly to become the coating liquid for the protective film on the surface of jewelry;

[0039] (2) Remove dust and oil on the surface of jewelry, and keep the surface of jewelry clean, oil-free and dry;

[0040] (3) In a dust-free and oil-free environment, use a spray gun to spray the coating liquid of the jewelry prote...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a jewelry surface protective film prepared by adopting the following raw materials according to parts by weight: 0.5-3 parts of aminopropyltriethoxysilane, 1-5 parts of Al2O3, 15-25 parts of SiO2, 20-30 parts of isopropanol and 35-42 parts of water. The preparation method of the jewelry surface protective film comprises the following steps: (1) adding 10-15 parts (by weight) of the isopropanol in SiO2 micro-powder, carrying out even stirring, then adding Al2O3 micro-powder and the aminopropyltriethoxysilane, then adding the rest isopropanol and the water for even stirring, and finally forming a coating solution of the jewelry surface protective film; (2) cleaning a jewelry surface; (3) coating the coating solution of the jewelry surface protective film on the jewelry surface; and (4) drying, i.e. forming a layer of hard protective film on the piece of jewelry. The protective film has the advantages of high hardness, good protection effect, good protection against easy damage, simple production process and low cost.

Description

technical field [0001] The invention belongs to the technical field of jewelry maintenance, and relates to a jewelry surface protective film and a manufacturing method thereof. Background technique [0002] At present, the commonly used jewelry surface protection mostly uses a layer of metal plating on the jewelry surface, such as gold, silver, platinum, copper, rhodium, etc., to prevent the wear and loss of luster on the jewelry surface. Although these materials are easy to mold, shape, and polish, this This kind of electroplating surface is actually easy to wear and lose luster, and the surface of electroplated jewelry is easily damaged, which will also reduce the life and value of jewelry, and this coating method is not suitable for the surface of gemstones, especially fragile gemstones. In addition, the electroplating process will produce a large amount of toxic pollutants, causing environmental pollution. Contents of the invention [0003] The technical problem to be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00B05D7/24A44C27/00
CPCB05D2203/30B05D1/02A44C27/005B05D3/12C23C26/00B05D7/14B05D5/00
Inventor 陈远陈遂
Owner 陈远