Thermal treatment method for precipitation hardening of martensitic stainless steel FV520B

A martensitic stainless steel, FV520B technology, applied in the field of heat treatment of precipitation hardened martensitic stainless steel FV520B, can solve the problems of low toughness in low temperature tempering, low strength in high temperature tempering, incompatibility of high strength and high toughness, etc., to achieve Effect of heat treatment on energy saving, strength and toughness improvement

Inactive Publication Date: 2009-08-19
NORTHEASTERN UNIV
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a heat treatment method for precipitation hardening martensitic stainless steel FV520B, so that the steel has excellent toughness and strength combination, and so

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A piece of FV520B precipitation hardening martensitic steel is selected. The main components of the steel are shown in Table 1. The original state of the steel is a forged plate with a thickness of (11)mm, and the characteristic temperature of the phase transformation of the steel is tested by a thermal dilatometer: A c1 、A c3 , Ms see Table 2. According to this, steel alloys were tempered at different temperatures and cooling methods, and their tensile properties and impact properties were compared.

[0023] Table 1 Main components of FV520B precipitation hardening martensitic steel

[0024] element C Si mn S P Ni Cr Cu Mo Nb content 0.042 0.335 0.579 0.0016 0.017 5.540 13.80 1.560 1.470 0.391

[0025] Table 2 Phase transformation characteristic temperature of FV520B precipitation hardening martensitic steel

[0026] critical point A c1 A c3 Mrs. temperature °C 589 847 180

[0027] The heat tr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Impact toughnessaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for heat-treating precipitation-hardened martensitic stainless steel FV520B, particularly a method adopting the following manner: tempering the precipitation-hardened martensitic stainless steel FV520B at a higher temperature for a short time and then slowly cooling, to lead the precipitation-hardened martensitic stainless steel FV520B to have the advantage of good combination of toughness and strength, and solve the following problems of the existing heat treatment processes: the high-temperature tempering strength is low and the low-temperature tempering toughness is low; as a result, the high strength and the high toughness cannot be achieved at the same time.

Description

technical field [0001] The invention relates to a heat treatment method of precipitation hardening martensitic stainless steel FV520B. Specifically, the precipitation hardening martensite is tempered at a relatively high temperature for a short time, and then slowly cooled to make the precipitation hardening martensite Stainless steel has an excellent combination of toughness and strength. Background technique [0002] Low-carbon precipitation-hardening martensitic stainless steel is widely used because of its easy processing, high strength, good toughness, excellent corrosion resistance and welding performance, good impact toughness and ideal transverse properties on larger sections Used in gears, bolts, shafts, discs, blades, rotors, pump parts, etc. Various components of this type of martensitic stainless steel with excellent performance have been successfully manufactured internationally. However, due to technical confidentiality and other reasons, the details of the ke...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21D6/00C21D1/28C21D1/00
Inventor 周倩青翟玉春
Owner NORTHEASTERN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka