Whole plant material environment friendly dishware and the process for making the same

A plant material and preparation technology, applied in the direction of the plate, etc., can solve the problems of poor performance and high production process requirements, and achieve the effect of convenient processing, low price and low water content

Inactive Publication Date: 2009-08-26
哈秋舲
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are also chemical glues such as acetone, epoxy resin, and industrial glue. Therefore, this kind of pr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Whole plant material environment friendly dishware and the process for making the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Raw material ratio:

[0026] 1,800 tons of flour, 180 tons of plant fiber with a length of 3 cm, and 100 tons of ordinary starch;

[0027] Preparation Process

[0028] (1) above-mentioned plant long fiber is mixed in edible powder, stirs;

[0029] (2) Stir evenly with an appropriate amount of normal temperature water and ordinary starch, and then stir with edible powder mixed with plant long fiber to form plasticity;

[0030] (3) compression molding;

[0031] (4) dry.

Embodiment 2

[0033] Raw material ratio:

[0034] 1600 tons of flour, 200 tons of plant fiber with a length of 1 cm, and 20 tons of konjac flour;

[0035] Preparation Process

[0036] (1) above-mentioned plant long fiber is mixed in edible powder, stirs;

[0037] (2) Stir with the edible powder mixed with plant long fiber after appropriate amount of normal temperature water and konjac powder are stirred into plasticity;

[0038] (3) compression molding;

[0039] (4) dry.

[0040] (5) Spray one layer of konjac powder liquid on the tableware surface after drying.

Embodiment 3

[0042] Raw material ratio:

[0043] 2,000 tons of flour, 300 tons of plant fiber with a length of 2 cm, and 20 tons of konjac flour;

[0044] Preparation Process

[0045] (1) above-mentioned plant long fiber is mixed in edible powder, stirs;

[0046] (2) Stir with the edible powder mixed with plant long fiber after appropriate amount of normal temperature water and konjac powder are stirred into plasticity;

[0047] (3) compression molding;

[0048] (4) dry.

[0049] (5) Spray one layer of konjac powder liquid on the tableware surface after drying.

[0050] In summary, the present invention modifies the edible powder with vegetable gum and mixes a small amount of plant long fiber, so the product has high strength, improved brittleness, anti-leakage, oil-proof, good temperature resistance and good usability. All are made of plant materials, no waste is discharged, and fully meet environmental protection requirements.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Whole plant material environment friendly dishware and the process for making the same are disclosed in the invention, which aims to solve the problem of chemical substances existing in the prior environment friendly dishware. The whole plant material environment friendly dishware of the invention is made by the following raw materials based on weight percentages: 80%-85% of food flour, 10%-15% of plant long fiber with the length of 1cm-3cm, and 5%-10% of vegetable gum. The process for making the whole plant material environment friendly dishware includes the following steps: (1) adding the plant long fiber into the food flour; (2) adding water and konjaku flour into the above mixture and agitating into plasticity substances; (3) compression molding; and (4) drying. According to the materials and the making process, the product strength is increased, the fragility is improved, the cost is reduced; in addition, the invention is convenient to produce, high in yield of finished product and is low in energy consumption during drying.

Description

technical field [0001] The invention relates to a production process of all plant material environment-friendly tableware Background technique: [0002] The production of plastic lunch boxes is first to heat the plastic, make a liquid mixture with a foaming agent, then spray it into a mold, and heat it to solidify. The production process is simple, the plastic is a polymer material, the physical performance is good, and the use is convenient. However, due to the extremely stable chemical properties of plastics, it is not easy to decompose. Extensive use once caused serious "white pollution". Therefore, the government has regulations to limit the use of plastic lunch boxes. [0003] However, some so-called environmentally friendly lunch boxes are now produced, and the materials used are basically plastic mixed with starch. The aim is to take advantage of the advantages of plastic, while starch can be decomposed, so that "white pollution" can be reduced. However, after th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A47G19/03C08L3/02C08L97/02
Inventor 哈秋舲
Owner 哈秋舲
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap