Polystyrene/polyethylene blended high-flame-resistance extruded sheet and production method thereof
A technology of polystyrene and polyethylene, which is applied in the field of high flame-retardant extruded plastic board and its preparation, can solve the problems that white pollution sources cannot be self-degraded, the flame-retardant effect cannot be achieved, and the product performance is poor, so as to improve hardness and improve Insulation effect, effect of improving product strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0023] Example 1: A polystyrene / polyethylene blended polystyrene / polyethylene blended high flame retardant extruded board includes the following components:
[0024]
[0025]
[0026] The carrier of the masterbatch is polyperfluoroethylene propylene.
[0027] The method for preparing the above-mentioned polystyrene / polyethylene blended high flame retardant extruded board includes the following steps:
[0028] (1) Add the decolorized polystyrene recycled material into the mixer, heat to 185°C under nitrogen, and add benzoyl peroxide and benzoyl peroxide, mix well and keep stirring Stop stirring after 3h and cool to 60℃;
[0029] (2) Add polystyrene virgin material, polyethylene, color masterbatch and polyethylene grafted zinc maleate to the system in step (1), and heat it to 230°C again under the condition of flowing nitrogen to mix evenly and Heat preservation and stirring for 1.5h, add decabromodiphenyl ether, silicon-based flame retardant, styrene-sodium acrylate and magnesium alum...
Example Embodiment
[0032] Example 2: Polystyrene / polyethylene blended polystyrene / polyethylene blended high flame retardant extruded board includes the following components:
[0033]
[0034] The carrier of the masterbatch is polyperfluoroethylene propylene.
[0035] The method for preparing the above-mentioned polystyrene / polyethylene blended high flame retardant extruded board includes the following steps:
[0036] (1) Add the decolorized polystyrene recycled material into the mixer, heat to 150°C under nitrogen, and add butyl peroxide and benzoyl peroxide, mix well and keep stirring Stop stirring after 2h and cool to 50℃;
[0037] (2) Add polystyrene virgin material, polyethylene, color masterbatch and polyethylene grafted zinc maleate to the system in step (1), and heat again to 180°C under nitrogen to mix uniformly and Keep the temperature and stir for 1 hour, add decabromodiphenyl ether, silicon-based flame retardant, styrene-sodium acrylate and magnesium aluminum hydrotalcite and continue to sti...
Example Embodiment
[0040] Example 3: Polystyrene / polyethylene blended polystyrene / polyethylene blended high flame retardant extruded board includes the following components:
[0041]
[0042]
[0043] The carrier of the masterbatch is polyperfluoroethylene propylene.
[0044] The method for preparing the above-mentioned polystyrene / polyethylene blended high flame retardant extruded board includes the following steps:
[0045] (1) Put the decolorized polystyrene recycled material into the mixer, heat to 200°C under nitrogen, and add benzoyl peroxide and benzoyl peroxide, mix well and keep stirring Stop stirring after 5h and cool to 80℃;
[0046] (2) Add polystyrene virgin material, polyethylene, masterbatch and polyethylene grafted zinc maleate to the system in step (1), and heat again to 250°C under nitrogen flow to mix evenly and Keep the temperature and stir for 2h, add decabromodiphenyl ether, silicon flame retardant, styrene-sodium acrylate and magnesium aluminum hydrotalcite and continue to stir f...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap