Continuous annealing process of deep drawing and extra-deep drawing steel plates

An annealing process and ultra-deep drawing technology, used in manufacturing tools, furnaces, heat treatment equipment, etc., can solve the problems of reducing the quality of home appliances and automobiles, low production efficiency, and poor furnace temperature uniformity.

Inactive Publication Date: 2009-08-26
耿凯
View PDF0 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In recent years, with the rapid development of China's national economic construction, the iron and steel industry has achieved world-renowned achievements, and the market demand for high-performance, high-precision cold-rolled thin plates (such as home appliance plates, automobile plates, etc.) has continued to increase. However, in the previous heat treatment process, these plates were mainly produced by bell annealing. This system has disadvantages such as low production efficiency, high energy consumption

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Continuous annealing process of deep drawing and extra-deep drawing steel plates
  • Continuous annealing process of deep drawing and extra-deep drawing steel plates
  • Continuous annealing process of deep drawing and extra-deep drawing steel plates

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The steel plate is cleaned before annealing, so that the content of rolling oil and iron powder on the surface of the steel plate is required to be less than 20mg / m 2 . The steel plate enters the continuous annealing furnace and walks at a speed of 150-350m / min, using H 2 Nitrogen-hydrogen mixed gas with a content of 3-5% is sprayed on the surface of the steel plate to protect the steel plate from oxidation, and at the same time heat the steel plate to 120-180°C.

[0017] The steel plate heating temperature, holding time, overaging temperature and time generally vary according to the material grade. The steel plate heating temperature of different steel types is shown in the following table:

[0018]

steel type

heating temperature

(℃)

Holding time

(S)

Overaging temperature

(℃)

aging time

(S)

DQ

760

45

400～460

90

DDQ-IF

820

60

400～460

120 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a continuous annealing process of deep drawing and extra-deep drawing steel plates. The steel plate is washed before annealing to cause the contents of rolling oil and iron power on the surface of the steel plate are less than 20mg/m; the steel plate is put into a continuous annealing furnace and walks at the speed of 150-350m/min, mixed gas of nitrogen and hydrogen is used to blow the surface of the steel plate to protect and prevent the steel plate from oxidation, and the steel plate is heated to 120-180DEG C; and then the steel plate is heated again to 750-880 DEG C and the heat is preserved for 40-70 S; then, the steel plate is cooled to 400-460 DEG C and the heat is preserved for 60-300 S to carry out overaging treatment; finally, the steel plate is cooled to normal temperature. Owing to the employment of overaging annealing process, carbide in the steel is fully precipitated, thus guaranteeing the needs of drawing properties and extra-deep drawing properties of plates for household electrical appliances and of automobile plates.

Description

Technical field: [0001] The invention relates to a technology for heat treatment of steel plates, in particular to a continuous annealing technology for deep-drawn and ultra-deep-drawn steel plates. Background technique: [0002] In recent years, with the rapid development of China's national economic construction, the iron and steel industry has achieved world-renowned achievements, and the market demand for high-performance, high-precision cold-rolled thin plates (such as home appliance plates, automobile plates, etc.) has continued to increase. However, in the previous heat treatment process, these plates were mainly produced by bell annealing. This system has disadvantages such as low production efficiency, high energy consumption, and poor furnace temperature uniformity, so that some properties of heat-treated steel plates cannot reach the performance of home appliance plates, automobile plates, etc. Compared with the industrially developed countries in the world, there i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21D9/48C21D1/26C21D1/74C21D11/00
Inventor 倪志荣耿凯
Owner 耿凯
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap