Thick steel plate for pressure vessel, method for manufacturing the same, use of the same
A technology for a pressure vessel and a manufacturing method, applied in the field of iron and steel materials, can solve problems such as not being able to fully meet actual needs, and achieve the effects of facilitating the implementation of a heat treatment process, excellent low-temperature impact toughness, and easy implementation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0043] Example 1
[0044] Smelt according to the chemical composition shown in Table 2, and cast into a steel billet. The steel billet is hot rolled at 1100 to 1250°C, and the hot rolling deformation is more than 80%. After the rolling, the steel plate is heat-treated, heated at 910°C and kept warm, and then immediately sprayed with water to quickly cool to below 200°C, and then tempered at 640°C. The thickness of the finished steel plate is 40mm.
Example Embodiment
[0045] Example 2
[0046] The embodiment is the same as in Example 1, wherein the heating temperature during the heat treatment is 930°C, the tempering temperature is 620°C, and the thickness of the finished steel plate is 20mm.
Example Embodiment
[0047] Example 3
[0048] The embodiment is the same as in Example 1, wherein the heating temperature during the heat treatment is 890°C, the tempering temperature is 670°C, and the thickness of the finished steel plate is 70mm.
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap