Environmental-friendly cement tile mixed with slag and preparation method thereof

A cement tile, environmentally friendly technology, used in manufacturing tools, ceramic molding machines, roofs using tiles/slate tiles, etc., can solve problems such as environmental pollution, and achieve the effect of protecting the environment and saving resources

Active Publication Date: 2010-01-13
CHINA BUILDING MATERIALS ACAD
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to reduce the cost of cement tile production and solve the problem of environmental pollution caused by slag, the present invention adopts the following technical solutions: an environmentally friendly cement tile mixed with slag is prepared by adding slag to the raw materials for ordinary cement tile production environmentally friendly cement tile

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmental-friendly cement tile mixed with slag and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1, preparation and performance testing of environment-friendly cement tile mixed with slag

[0026] The following method is used to prepare the slag cement tile, and the specific method includes the following steps:

[0027] 1) Weighing and taking materials: 15kg of slag (fineness modulus 3.9), 100kg of ordinary Portland cement (P.O42.5 model, purchased from Hebei Jidong Cement Group Co., Ltd.), river sand (fineness The modulus is 2.5) 135kg, PowderA 0.12kg, water 26kg, mix the above raw materials evenly to form a wet material;

[0028] 2) Fill the wet material into a standard mold and press it into shape; the pressure is 10MPa, and the pressurization time is 3 seconds;

[0029] 3) Standard maintenance: After demoulding, maintain for 24 hours without water, and then soak in water for maintenance;

[0030] An environment-friendly cement tile mixed with slag is obtained.

[0031] The environment-friendly cement tile mixed with slag of the present invention i...

Embodiment 2

[0036] Example 2, Preparation and performance testing of environmentally friendly cement tiles mixed with slag

[0037] The following method is used to prepare the environment-friendly cement tile mixed with slag, and the specific method includes the following steps:

[0038] 1) Weighing and taking materials: 60kg of slag (fineness modulus of 3.5), 80kg of sulphoaluminate cement (R-SAC42.5 model, purchased from Tangshan Liujiu Cement Co., Ltd.), river sand (fineness modulus of 2.3) 110kg, 1.0kg calcium stearate, 20kg water, mix the above raw materials evenly;

[0039] 2) Compression molding; pressure 20MPa, pressure hold time 2 seconds;

[0040] 3) Standard maintenance: After demoulding, maintain for 24 hours without watering, and then watering for curing.

[0041] An environment-friendly cement tile mixed with slag is obtained.

[0042] The environment-friendly cement tile mixed with slag of the present invention is tested according to the performance testing method in the...

Embodiment 3

[0045] Example 3, Preparation and performance testing of environmentally friendly cement tiles mixed with slag

[0046] The following method is used to prepare the environment-friendly cement tile mixed with slag, and the specific method includes the following steps:

[0047] 1) Weighing and taking materials: 5 kg of slag (fineness modulus 4.0), 130 kg of ordinary Portland cement (P.O42.5 model, purchased from Hebei Jidong Cement Group Co., Ltd.), river sand (fineness The modulus is 3.0) 115kg, water 39kg, mix the above-mentioned raw materials evenly;

[0048] 2) Compression molding; pressure 6MPa, pressurization hold time 3 seconds;

[0049] 3) Standard maintenance: After demoulding, it is maintained for 24 hours without water, and then naturally cured;

[0050] An environment-friendly cement tile mixed with slag is obtained.

[0051] The environment-friendly cement tile mixed with slag of the present invention is tested according to the performance testing method in the "Co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Fineness modulusaaaaaaaaaa
Fineness modulusaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environmental-friendly cement tile mixed with slag and a preparation method thereof. The environmental-friendly cement tile is prepared by adding slag on the basis of a common cement tile raw material and comprises the following raw materials: 5-60 parts of slag, 80-130 parts of cement, 75-165 parts of sand, 0-1.6 parts of water repellent and 20-39 parts of water. Tests prove that the slag added into the cement tile leads the breaking strength of the cement tile to meet the standard requirement and can consume waste residues generated after a plurality of lump coal or pea coal is burnt; and the invention utilizes the waste, saves resources and protects the environment. The invention plays an important role in the field of construction and has wide market prospect.

Description

technical field [0001] The invention relates to the field of building materials, and mainly relates to the reuse of industrial waste, in particular to an environment-friendly cement tile mixed with slag and a preparation method thereof. Background technique [0002] my country is a large coal-producing country. In recent years, my country's energy industry has developed steadily. The loose or lumpy residue after burning lump coal or granular coal that has not been quenched by water has become one of the industrial wastes with a large discharge volume in my country. With a large amount of emissions increasing year by year, these slags have not been recycled, which has caused huge pressure on my country's national economic construction and ecological environment. [0003] Cement tiles (also known as concrete tiles) have a long history. This industry is one of the most traditional, low-investment and widely distributed production industries in China. The usual cement tiles use ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04D1/00B28B3/00B28B11/24C04B28/00C04B28/04C04B28/36C04B18/10
CPCC04B2111/00017C04B28/02Y02W30/91C04B14/06C04B18/067C04B24/085
Inventor 李清海孙蓓
Owner CHINA BUILDING MATERIALS ACAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com