Process method for manufacturing metallographic specimen

A process method and metallographic sample technology, applied in the preparation of test samples, manufacturing tools, metal processing equipment, etc., can solve problems such as low efficiency, and achieve the effects of ensuring the quality of sample preparation, saving costs, and improving efficiency

Active Publication Date: 2010-04-07
CHENGDE JIANLONG SPECIAL STEEL
View PDF0 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The traditional metallographic sample preparation adopts manual grinding, which is inefficient. The mechanical sample must be subjected to precision grinding (that is, flat grinding). The metallographic tester spreads metallographic sandpaper on the glass plate and manually 4-5 st

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The present invention will be further described in detail according to the examples below.

[0014] A kind of technological method of metallographic sample preparation is characterized in that, comprises the steps:

[0015] a) Rapid grinding of sawing samples: Use a spectroscopic decommissioned sample grinding machine changed to a grinding wheel grinding disc, use a grinding fixture that can hold 8-10 samples at a time to quickly grind samples, hold it by hand, and perform rapid grinding on the sample grinding machine. Grinding, surface roughness to Ral.6-0.8um, meeting the requirements of precision grinding;

[0016] b) Metallographic grinding sample: The metallographic grinding and polishing machine can realize stepless speed change; the cold mounting resin composed of acid anhydride hardener and epoxy aliphatic resin with a ratio of 1:2 is used to fill the concave of the grinding disc of the grinding and polishing machine. Groove, to achieve the hardness suitable fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a process method for manufacturing a metallographic specimen, which comprises the following steps: a) quickly grinding a saw-cut specimen, wherein a spectrum-decommissioning specimen grinding machine changed into an abrasive wheel grinding plate is used; and a specimen grinding fixture which can clamp 8 to 10 specimens once is utilized to quickly grind the specimens and is manually held to quickly grind the specimens on the specimen grinding machine until surface roughness reaches to Ra 1.6 to 0.8 microns so as to meet the requirements on precise grinding; b) performing metallographic specimen grinding; and c) performing metallographic polishing. Compared with the prior art, the process method for manufacturing the metallographic specimen in the invention has the advantages of conveniently and quickly manufacturing the metallographic specimen, and not only ensuring the specimen manufacturing quality and analysis quality, but also saving the cost and improving the efficiency.

Description

technical field [0001] The invention relates to a process method for making a metallographic sample. Background technique [0002] The production of metallographic samples (grinding, polishing, processing) accounts for about 2 / 3 of the total time of metallographic analysis, so how to improve the efficiency of metallographic sample preparation is of great significance. [0003] The traditional metallographic sample preparation adopts manual grinding, which is inefficient. The mechanical sample must be subjected to precision grinding (that is, flat grinding). The metallographic tester spreads metallographic sandpaper on the glass plate and manually 4-5 steps of grinding, the grain size of the sandpaper is getting finer and finer, grinding from (180#-)240#-400#-600#-800# in sequence, the fine grinding sample needs to be increased to 1000# or even 1200#, and every Replace a piece of sandpaper, and clean the sample and table at the same time. After the grinding process is compl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N1/28G01N1/32B24B7/16B24B29/02
Inventor 姚忠朱丽萍姜彩艳董孟宪
Owner CHENGDE JIANLONG SPECIAL STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap