Method for preparing black zirconia ceramics at low temperature

A technology of black zirconia and ceramics, which is applied in the field of preparation of low-temperature sintered black zirconia ceramic materials, which can solve the problems of material strength, hardness and corrosion resistance reduction, and achieve the goal of avoiding toxic effects, large specific surface area and narrow size distribution. Effect

Inactive Publication Date: 2010-05-12
TSINGHUA UNIV
View PDF0 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, since the present invention does not add sintering aids, it overcomes the disadvantages of reducing material strength, hardness and corrosion resistance caused by sintering aids in conventional preparation methods.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing black zirconia ceramics at low temperature
  • Method for preparing black zirconia ceramics at low temperature
  • Method for preparing black zirconia ceramics at low temperature

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Black ZrO 2 Preparation of ceramics:

[0036] (1) Raw material preparation: zirconium oxychloride ZrOCl 2 ·8H 2 O and Y (NO 3 ) 3 ·6H 2 O is the raw material, and ZrOCl with a concentration of 0.2mol / L is prepared with secondary deionized water 2 -Y(NO 3 ) 3 solution and a 10% ammonia solution. ZrOCl 2 -Y(NO 3 ) 3 Solution according to n(ZrO 2 ) / n(Y 2 o 3 )=97 / 3. A certain amount of deionized water, ammonia water, dispersant polyethylene glycol and 6-10% solution weight hydrogen peroxide are taken as the reaction base liquid, and the pH value of the reaction base liquid is adjusted to 10. Stir the reaction base solution continuously at room temperature, and drop the two solutions prepared above (ZrOCl 2 -Y(NO 3 ) 3 solution and ammonia solution), after the dropwise addition, the stirring was continued for 1 hour, and a white sol precipitate was obtained. Stand and age at room temperature for 10 hours, use a centrifuge to separate the solid from the li...

Embodiment 2

[0052] Black ZrO 2 Preparation of ceramics:

[0053] Raw material ZrO 2 , coloring agent and green body preparation method are basically the same as embodiment one. The difference: the added amount of the coloring agent is 2wt% and 0wt%.

[0054] Characterization method:

[0055] The phase analysis of the material was carried out with the Regaku D / max X-ray diffractometer (CuKα line) of Japan; the microstructure of the sample was observed with the SSX-550 scanning electron microscope; the AG-1C type of the Shimadzu universal material testing machine was used to determine the Bending strength; test the Vickers hardness of the sample with the HV-50 Vickers hardness tester; test the bulk density of the sample with the Archimedes drainage method; soak the sample in 20% hydrochloric acid and sodium hydroxide solution for 48 hours, wash and observe Changes in surface color and gloss to evaluate its corrosion resistance.

[0056] result:

[0057] 1. Black ZrO 2 ceramic structure...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
flexural strengthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing black zirconia ceramics at the low temperature and belongs to the technical field of the preparation of high-temperature structural material. The method respectively uses a homogeneous precipitation method for synthesizing a nanometer coloring agent, and a coprecipitation method for synthesizing nanometer zirconia powder, and adopts Fe-Co-Ni-Mn as a coloring agent. The zirconia powder is not added with any sintering additive, only added with small amount of coloring agent and sintered at the temperature of 1150-1350 DEG C, thus obtaining the black zirconia ceramics with excellent performance and bright color. As the homogeneous precipitation method is adopted for synthesizing coloring agent powder, the monodisperse nanometer particles with uniform powder granules, narrow size distribution and high purity are obtained so that the coloring agent easily colors the particles. As the coprecipitation method is used for synthesizing zirconia powder, nanometer particles with small granularity, big superficial area and high activity are obtained, and can reduce the temperature of the solid-phase reaction, greatly reduce the sintering temperature and solve the problem that the black coloring agent oxide decomposes and volatiles at the high temperature. Simultaneously the method adopts the Fe-Co-Ni-Mn as the coloring agent, thus avoiding the poisonous function of Cr on the human body.

Description

technical field [0001] The invention relates to a method for preparing a low-temperature sintered black zirconia ceramic material, which belongs to the technical field of high-temperature structural material preparation. Background technique [0002] Zirconium dioxide is widely used and researched in high-temperature structural materials, high-temperature optical components, oxygen-sensitive components, fuel cells, etc. . In recent years, with the rapid development of people's demand for decorations, black ZrO 2 With its excellent mechanical properties, bright colors, metallic luster, and non-allergic effects, ceramics have become the new favorite materials for high-end decoration, such as high-end watch chains, bracelets, and mobile phone casings. Therefore, the research and development of black zirconia ceramics has broad market prospects. [0003] As we all know, the preparation of ordinary black ceramics is generally obtained by adding pigment or colorant to the ceram...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/48C04B35/622
Inventor 司文捷吴音
Owner TSINGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com