High-strength stretch-proof flame-retardant textile

A flame-retardant fabric, stretch-resistant technology, applied in the direction of fabrics, textiles, textiles and papermaking, can solve the problems of insufficient softness, easy to break, etc. Effect

Inactive Publication Date: 2010-06-23
汕头市奥山服饰有限公司
View PDF2 Cites 68 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The inorganic fibers that play the role of cut resistance are metal fibers, so this fabric is very hard, not soft enough, and easy to break, not ideal for clothing or mattresses, seat fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The high-strength stretch-resistant flame-retardant fabric described in this embodiment is a flame-retardant fabric for welding protective clothing.

[0022] A flame-retardant fabric for welding protective clothing is woven from a flame-retardant composite yarn, wherein the flame-retardant composite yarn is composited by a core yarn and a skin yarn; the flame-retardant composite yarn is a core-spun yarn; the flame-retardant composite yarn is a core-spun yarn; In the core-spun yarn, the sheath yarn is the outer fiber; the core yarn is made of flame-retardant filament raw material, and the sheath yarn is made of ordinary flame-retardant short fiber raw material; the flame-retardant filament is para-aramid fiber, so The common flame-retardant short fibers are melamine fibers; the weight ratio of the para-aramid fibers to the melamine fibers can be selected in the range of 30-90: 10-70, and the preferred weight ratio is 40: 60; the fineness of the flame retardant composite ...

Embodiment 2

[0030] The high-strength stretch-resistant flame-retardant fabric described in this embodiment is a flame-retardant protective clothing fabric.

[0031] A flame-retardant protective clothing fabric is woven from a flame-retardant composite yarn, wherein the flame-retardant composite yarn is composited by a core yarn and a skin yarn; the flame-retardant composite yarn is a wrapping yarn, and the wrapping yarn The skin yarn in the wrapping yarn is the outer yarn; the core yarn is made of flame-retardant filament raw material, and the skin yarn is made of ordinary flame-retardant short fiber raw material; the flame-retardant filament is meta-aramid fiber, so The common flame-retardant short fibers are acrylic fibers; the weight ratio of the meta-aramid fibers to the acrylic fibers can be selected in the range of 30-90: 10-70, and the preferred weight ratio is 70:30; the fineness of the flame retardant composite yarn is 15tex; the square meter mass of the flame retardant protectiv...

Embodiment 3

[0038] The high-strength stretch-resistant flame-retardant fabric described in this embodiment is a train seat flame-retardant fabric.

[0039] A flame-retardant fabric for train seats is woven from a flame-retardant composite yarn, wherein the flame-retardant composite yarn is composed of a core yarn and a skin yarn; the flame-retardant composite yarn is a core-spun yarn, and the flame-retardant composite yarn is a core-spun yarn. In the core-spun yarn, the sheath yarn is the outer fiber; the core yarn is made of flame-retardant filament raw material, and the sheath yarn is made of ordinary flame-retardant short fiber raw material; the flame-retardant filament is polysulfone-based amide fiber, so The common flame-retardant short fibers are flame-retardant polyester fibers; the weight ratio of the polysulfone-based amide fibers and the flame-retardant polyester fibers can be selected within the range of 30-90:10-70, and the preferred weight ratio is is 50:50; the fineness of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
smoldering timeaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-strength stretch-proof flame-retardant textile. The flame-retardant textile is formed by weaving a flame-retardant composite yarn, wherein the flame-retardant composite yarn is formed by compounding a core yarn and a leather yarn and is one of a covering yarn and a fasciated yarn; the core yarn adopts a flame-retardant filament yarn as a raw material; the leather yarn adopts a flame-retardant short fiber as a raw material; and the weight ratio of the flame-retardant filament yarn to the flame-retardant short fiber is 30-90:10-70. Compared with the conventional flame-retardant textile, the high-strength stretch-proof flame-retardant textile has higher strength and overcomes the defects of difficult weaving, difficult dyeing and uncomfortableness of the high-strength fiber; the high-strength stretch-proof flame-retardant textile has permanent flame retardance which cannot decrease after the textile is washed, and better textile strength; the textile has soft and comfortable handfeel, rich color and good strength, meets the requirements of various flame-retardant clothes and related standards; the product has rich and varied appearances and is durable; and the combustion performance of the textile can meet the national standards of flame-retardant products.

Description

technical field [0001] The invention relates to a high-strength stretch-resistant flame-retardant fabric. The flame-retardant fabric is woven from a flame-retardant composite yarn; the flame-retardant composite yarn is composited from a core yarn and a skin yarn; The composite yarn is one of a core-spun yarn and a wrap-around yarn; the core yarn is made of flame-retardant filament raw material, and the skin yarn is made of flame-retardant short fiber raw material. Background technique [0002] With the development of my country's economy, frequent reports of fires in various places, people's awareness of fire prevention has gradually increased, and relevant national laws, regulations and standards have been promulgated one after another, and the requirements and demands for fire-retardant and flame-retardant fabrics have also increased year by year. At present, with the continuous progress of science and technology, the gradual improvement of industrial production and manufa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/12D02G3/36D02G3/04D03D15/225D03D15/242D03D15/283D03D15/40D03D15/47D03D15/513D03D15/573
Inventor 吴汉荣
Owner 汕头市奥山服饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap