Enhancing agent for consolidating tailing of iron core

A technology of iron ore tailings and reinforcing agent, which is applied in the field of curing reinforcing agent, and can solve problems such as increasing project cost

Active Publication Date: 2010-07-21
吉林中路新材料有限责任公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to meet the requirements of the iron ore tailings structure on the pavement base, it is often necessary to add a large amount of cement to meet the needs of the project, which will greatly increase the project cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] For iron ore tailings in Chaoyang City, Liaoning Province, the main reinforcing agents are sodium methyl siliconate 12%, USZ 8%, Na 2 SO 4 15%, sodium aluminate 12%, sodium succinate sulfonate 3%, water 50%.

[0026] (1) Seven-day unconfined compressive strength 3.1MPa

[0027] (2) Bending and tensile strength 0.62MPa

[0028] (3) Rebound modulus 1600MPa

Embodiment 2

[0030] Sodium Methyl Siliconate 7%, USZ 13%, Na 2 SO 4 10%, sodium succinate sulfonate 5%, sodium aluminate 15%, water 50%.

[0031] (1) Seven-day unconfined compressive strength 3.3MPa

[0032] (2) Bending and tensile strength 0.62MPa

[0033] (3) Rebound modulus 1700Mpa

Embodiment 3

[0035] Sodium Methyl Siliconate 10%, USZ 9%, Na 2 SO 4 25%, sodium succinate sulfonate 1%, sodium aluminate 5%, water 50%.

[0036] (1) Seven-day unconfined compressive strength 3.0MPa

[0037] (2) Bending and tensile strength 0.5MPa

[0038] (3) The modulus of resilience is 1350Mpa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an enhancing agent for consolidating tailing of iron core, which is composed of 7-12% of sodium methylsilanolate, 8-13% of acetonformaldehyde condensate sulfonate (USZ), 10-25% of NaSO4, 1-5% of succinate sodium, 5-15% of sodium aluminate and 50% of water. The product has no harm to human body, livestock and plants. The soil solidified intensifier has high initial strength, good cracking resistance and freeze resistance, the seven-day unconfined compression strength is larger than or equal to 3.0Mpa, the anti-bending tensile strength is 0.50-0.62Mpa, the modulus of resilience is 1,300-1,700Mpa, and the water stability is 90-95%. The intensifier has less usage and large supply diameter, facilitates construction and can reduce construction cost.

Description

technical field [0001] The invention belongs to a solidification enhancer using iron ore tailings as road construction materials, which is suitable for roadbed construction in road engineering. It has the advantages of improving the mechanical properties of the subgrade and water resistance. Background technique [0002] The reinforcing agent of the invention is a novel chemical material used to improve iron ore tailings as road construction. It can significantly improve the mechanical properties of iron ore tailings and cement consolidated roadbed with large pores and poor gradation. Referring to the road construction technology of sandy soil and gravel soil, the soil solidification technology can be divided into the following categories: [0003] (1) Inorganic binder [0004] Inorganic binder is a traditional solidifying material, including cement, lime and fly ash, etc. They can be used alone or mixed in a certain proportion. Cement, lime, and fly ash are widely used ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/42
Inventor 王汝堂轩景泉王立志
Owner 吉林中路新材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap