Coating compositions comprising organofunctional polysiloxane polymers, and use thereof

A polysiloxane, composition technology, applied in anti-corrosion coatings, biocide-containing paints, antifouling/underwater coatings, etc.

Active Publication Date: 2013-11-06
佐顿公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But molecular simulations unexpectedly show that at similar crosslink densities, carbon-based meshes also become tense and brittle

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating compositions comprising organofunctional polysiloxane polymers, and use thereof
  • Coating compositions comprising organofunctional polysiloxane polymers, and use thereof
  • Coating compositions comprising organofunctional polysiloxane polymers, and use thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0120] The following examples are used to further illustrate the present invention.

[0121] Examples related to aggregation

[0122] polymer preparation

[0123] Table 1 Amino-functional polysiloxanes prepared according to the present invention

[0124] CAS N. 1 2 3 4 5 6

[0125] [g] [g] [g] [g] [g] [g] Dialkoxy functional silane Aminopropylmethyldiethoxysilane 3179-76-8 30 60 Aminoethylaminopropylmethyldimethoxysilane 3069-29-2 25 75 50 50 Trialkoxy functional silane Aminopropyltriethoxysilane 919-30-2 20 Monoalkoxy functional silane Trimethylethoxysilane 1825-62-3 10 10 10 10 10 10 other materials Triethylamine (catalyst) 121-44-8 Cyclohexanone 108-94-1 5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a coating composition comprising an organofunctional polysiloxane polymer as a binding resin, obtaining the polymeric structure as part of a curing mechanism or a combination thereof. The main advantage of the invention is that it enables the formation of a flexible inorganic polymeric structure that is more UV-light, heat and oxidation resistant than a coating comprising a large percentage of a carbon based organic polymer.

Description

technical field [0001] The present invention relates to a coating composition or mixture thereof comprising an organofunctional polysiloxane polymer as a binder resin which acquires a polymeric structure as part of the curing mechanism. [0002] A major advantage of the present invention is that it facilitates the formation of a flexible inorganic polymeric structure that is more resistant to UV light, heat and oxidation than coating compositions containing high proportions of organic carbon-based polymeric materials. Background technique [0003] Generally, polysiloxane polymers are considered to be highly resistant to heat, light, and oxidation, but tend to be brittle when applied as a quantitatively three-dimensional crosslinked network. According to the prior art, this problem is solved by mixing more flexible organic polymers in the polysiloxanes. On the other hand, organic polymers generally have poor resistance to heat, ultraviolet light, and oxidation, so that the r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/04C09D183/06C09D5/16C09D5/00C08L83/04C08L83/06
CPCC09D5/1675C09D5/08C09D183/04C09D183/06C08K5/5419C08L2666/44C08L83/04C09D5/16
Inventor 希古·尼尔森
Owner 佐顿公司