Vacuum thermal baffle packaging film and preparation method thereof
A vacuum heat insulation board and packaging film technology, applied in packaging, wrapping paper, transportation and packaging, etc., can solve the problems of affecting the heat insulation effect of finished VIP boards, affecting the appearance of VIP boards, and difficult production processes, etc., to achieve good physical Good mechanical properties, peel strength, and good aging resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0036] Example 1:
[0037] Vacuum insulation board packaging film, such as figure 1 Shown: Its production process is as follows:
[0038] a. Printing process: printing on biaxially oriented nylon film at 20-30°C;
[0039] b. The preparation process of composite polyethylene; each layer of polyethylene resin is placed in their respective barrels for extrusion according to a specific addition ratio to form a composite polyethylene film; image 3 As shown: the composite polyethylene layer is composed of a composite outer layer 51, a core layer 52, and a heat-sealed inner layer 53 in order from the outside to the inside;
[0040] c. The first dry laminating process: the biaxially oriented nylon film and polyethylene terephthalate film that have been printed with patterns are combined by a dry laminating machine, and then the composite biaxially oriented nylon film / Polyethylene terephthalate film and aluminum foil are dry composited to form a biaxially stretched nylon / polyethylene tereph...
Example Embodiment
[0056] Example 2:
[0057] Except in b, the preparation process of composite polyethylene.
[0058] Composite outer layer: 45% m-LLDPE DOW5100 (produced by Dow Chemical Company);
[0059] 45% MDPE 2038.68G (produced by Dow Chemical Company);
[0060] 10% LDPE150BW (produced by ExxonMobil);
[0061] Core layer: 60% HDPE HTA108 (produced by ExxonMobil);
[0062] 40% m-LLDPE 1018FA (produced by ExxonMobil);
[0063] Layer C: 30% LDPE 150BW (produced by Exxon Mobil);
[0064] 70% m-LLDPE PL1881G (produced by The Dow Chemical Company);
[0065] Except for the ±5% limit deviation of the produced composite polyethylene, the rest is the same as in Example 1.
Example Embodiment
[0066] Example 3:
[0067] Except in b, the preparation process of composite polyethylene.
[0068] Composite outer layer: 30% m-LLDPE DOW5100 (produced by Dow Chemical Company);
[0069] 50% MDPE 2038.68G (produced by Dow Chemical Company);
[0070] 20% LDPE150BW (produced by ExxonMobil);
[0071] Core layer: 50% HDPE HTA108 (produced by ExxonMobil);
[0072] 50% m-LLDPE 1018FA (produced by ExxonMobil);
[0073] Layer C: 40% LDPE 150BW (produced by Exxon Mobil);
[0074] 60% m-LLDPE PL1881G (produced by Dow Chemical Company);
[0075] The made composite polyethylene has a ±5% limit deviation; the rest is the same as in Example 1.
[0076] The main technical indicators of Examples 1-3 are as follows:
[0077]
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap