Halogen-free flame-retardant glassfiber reinforced PC/PBT alloy material and preparation method thereof

A technology of alloy material and PBT resin, which is applied in the field of halogen-free flame-retardant glass fiber reinforced PC/PBT alloy material and its preparation, can solve the problems of serious floating fibers on the surface of the workpiece, the appearance of flowers, and no use, etc., and achieve the improvement of the surface of the workpiece , Improve compatibility and improve fluidity

Inactive Publication Date: 2010-11-03
SHENZHEN KEJU NEW MATERIAL
View PDF5 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Ordinary glass fiber reinforced PC material has serious floating fibers on the surface of the part, and the appearance is very flowery. The surface is a layer of white glass fiber texture, and it is generally not used for appearance parts.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] PC 2805 resin 65 parts, PBT 1100 resin 10 parts, compatibilizer KT-201 parts, toughening agent POE 4 parts, halogen-free flame retardant FRMB50103 parts, glass fiber 303H 15 parts, coupling agent KH-5500.5 parts, lubrication 1 part of anti-oxidant, 10100.2 parts of 1680.3 parts of antioxidant.

[0036] Preparation:

[0037] Weigh the above raw materials;

[0038] Dry PC resin and PBT resin in a blower dryer at a temperature of 110°C to 130°C for 3 to 5 hours, and compatibilizer, toughener, halogen-free flame retardant, coupling agent, lubricant, Antioxidants are mixed evenly in the mixing tank;

[0039] The mixed raw materials are placed in the feeding barrel of the extruder, melted and extruded by the twin-screw extruder, and granulated; the short glass fiber is added at the side feeding port, and the process parameters of the twin-screw extruder are: one zone Temperature 245~235℃, temperature in zone 2 240~230℃, temperature in zone 3 235~225℃, temperature in zone 4...

Embodiment 2

[0041] PC 2805 resin 57 parts, PBT 1100 resin 15 parts, compatibilizer KT-201 parts, toughening agent POE 5 parts, halogen-free flame retardant FRMB50105 parts, glass fiber 303H 15 parts, coupling agent KH-5500.5 parts, lubrication 1 part of anti-oxidant, 10100.3 parts of 1680.2 parts of antioxidant.

[0042] The preparation method is the same as in Example 1.

Embodiment 3

[0044]PC 2805 resin 53 parts, PBT 1100 resin 20 parts, compatibilizer KT-202 parts, toughening agent POE 5 parts, halogen-free flame retardant KSS 3 parts, glass fiber 303H 15 parts, coupling agent KH-5500.5 parts, 1 part lubricant, 10100.2 parts 1680.3 parts antioxidant.

[0045] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a halogen-free flame-retardant glassfiber reinforced polycarbonate / polybutylene terephthalate (PC / PBT) alloy material and a preparation method thereof. The halogen-free flame-retardant glassfiber reinforced PC / PBT alloy material consists of the following components in percentage by weight: 53 to 66.6 percent of PC resin, 10 to 20 percent of PBT resin, 1 to 2 percent of compatilizer, 3 to 5 percent of toughening agent, 1 to 5 percent of halogen-free flame retardant, 10 to 20 percent of glass fiber, 0.3 to 0.8 percent of coupling agent, 0.6 to 1 percent of lubricant and 0.2 to 0.5 percent of antioxidant. The halogen-free flame-retardant glassfiber reinforced PC / PBT alloy material of the invention has the advantages of high melt fluidity, bright and clean surface of product, and good comprehensive performance and can be used for manufacturing liquid crystal inner frames, television modules and some external products having high surface requirements.

Description

[technical field] [0001] The invention relates to the technical field of polymer materials, in particular to a halogen-free flame-retardant glass fiber reinforced PC / PBT alloy material and a preparation method thereof. [Background technique] [0002] PC (polycarbonate) resin is a thermoplastic engineering plastic with excellent performance, which has excellent transparency and outstanding impact resistance, good creep resistance and dimensional stability, heat resistance, low water absorption, non-toxic, dielectric With excellent performance, it is the only product with good transparency among the five major engineering plastics, and it is also the general engineering plastic with the fastest growth rate in recent years. At present, it is widely used in automobiles, electronics, construction, office equipment, packaging, sports equipment, medical care and other fields. With the continuous deepening of modification research, it is rapidly expanding to high-tech fields such as...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L69/00C08L67/02C08K13/04C08K7/14C08K5/42
Inventor 徐东贺永付天英
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products