Compatible accelerating agent of silicon dioxide coated aluminum paste and PVDF (Polyvinylidene Fluoride) high-fluorine emulsion and compatible method

A technology of silicon dioxide and accelerator, applied in the direction of coating, can solve the problems of coarse blackening and soft particles, no metal texture, rough paint film and loss of gloss, etc., to achieve improved miscibility, strong flickering feeling, and fine hand feeling Effect

Inactive Publication Date: 2010-11-24
安徽本雅明涂料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But when this aluminum paste is added to PVDF high-fluorine emulsion, it will turn coarse and black and produce soft particles that cannot be filtered out. The final paint film is often rough and dull, without metallic texture
The current technical system has three shortcomings: 1. A large amount of alcohol ether solvents are used to disperse the aluminum paste, such as: BCS, propylene glycol methyl ether, etc., which do not conform to the direction of environmental protection and low carbon; 2. The dispersed aluminum paste and PVDF high-fluorine emulsion Poor compatibility, thickening and blackening
3. The decorative effect of the paint film is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The present invention is described in further detail below in conjunction with embodiment.

[0023] The compatible accelerator of silica-coated aluminum paste and PVDF high-fluorine emulsion, and utilize this compatible accelerator to promote silica-coated aluminum paste and the compatible method of PVDF high-fluorine emulsion as following example:

[0024] 1) Add a surfactant / alcohol solution accounting for 10-40% of its solid content to nano colloidal silicon with a particle size of 10-15nm to obtain a compatibility accelerator;

[0025] 2) According to 2-9% of the solid content of the required PVDF high-fluorine emulsion, part of the compatibility accelerator is reserved for use;

[0026] 3) Measure whether the pH value of the remaining compatibility accelerator is between 8-10; if not within this range, adjust the pH value of the compatibility accelerator to between 8-10;

[0027] 4) At a stirring speed of 300-500rpm, slowly add the silica-coated aluminum paste to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a compatible accelerating agent of silicon dioxide coated aluminum paste and PVDF (Polyvinylidene Fluoride) high-fluorine emulsion and a compatible method for accelerating the compatibility of the silicon dioxide coated aluminum paste and the PVDF high-fluorine emulsion by using the compatible accelerating agent. By using nanometer colloidal silica and surfactant / alcohol solution as the compatible accelerating agent, the invention can greatly improve the miscibility of the silicon dioxide coated aluminum paste and the PVDF high-fluorine emulsion, has no phenomena of the thickening and the darkening of the aluminum paste and no soft particles incapable of filtering. The prepared paint film has exquisite hand feel, strong sparkling sense and metal quality. In addition, the compatible accelerating agent is used while a large quantity of alcohol ether organic solvents are unnecessary to use, thereby the invention satisfies the concept of environment protection and low carbon.

Description

technical field [0001] The invention relates to the field of water-based environmental protection coatings, in particular to an accelerator for promoting the compatibility of silica-coated aluminum paste and PVDF high-fluorine emulsion, and using the compatibility accelerator to promote the compatibility of silica-coated aluminum paste and PVDF high-fluorine emulsion Emulsion compatibility method. Background technique [0002] Usually, the silica-coated aluminum paste must be infiltrated by the solvent system to be well dispersed with the help of a wetting and dispersing agent. But when this aluminum paste is added to PVDF high-fluorine emulsion, it will turn coarse and black and produce soft particles that cannot be filtered out, and the final paint film is often rough and dull, without metallic texture. The current technical system has three shortcomings: 1. A large amount of alcohol ether solvents are used to disperse the aluminum paste, such as: BCS, propylene glycol me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D7/12C09D127/16
Inventor 叶聪
Owner 安徽本雅明涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com