Cationic dye chromophilous copolyester fibre dyeing assistant and dyeing method using same

A cationic dye and copolyester technology, which is applied in the field of fiber dyeing aids and dyeing with it, can solve the problems of hard hand feeling, poor deep dyeing effect of fibers, and restrictions on the development and marketing of Paiste fiber, and achieve low Effect of COD and energy reduction

Inactive Publication Date: 2010-11-24
嘉善嘉胜绢纺股份有限公司
View PDF5 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the deep dyeing effect of this fiber is poor, especially when it is dyed black, the polarization phenomenon is serious, and adding dyes will not help it. The larger the dye ratio is, the more serious the polarization will be, and the fabric produced with this fiber will feel hard after dyeing
It is precisely because of these two major defects that seriously restrict the development and marketing of Paxter fiber downstream products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cationic dye chromophilous copolyester fibre dyeing assistant and dyeing method using same
  • Cationic dye chromophilous copolyester fibre dyeing assistant and dyeing method using same
  • Cationic dye chromophilous copolyester fibre dyeing assistant and dyeing method using same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Cationic dye easy-to-dye copolyester fiber dyeing aid formula:

[0037] Diethylene glycol dibenzoate 45%

[0038] Macrogol 400 35%

[0039] Cetyltrimethylammonium Bromide 10%

[0040] Castor Oil Polyoxyethylene Ether EL-40 10%

[0041] Preparation method: Add cetyltrimethylammonium bromide and castor oil polyoxyethylene ether EL-40 into a blender, heat while stirring, when the temperature rises to 55°C, add polyethylene glycol under slow stirring 400, and then add diethylene glycol dibenzoate under slow stirring to obtain a light yellow transparent liquid, which is lowered to room temperature while stirring to obtain a stable liquid. The cationic dye easy-to-dye copolyester fiber dyeing aid of the present invention can be obtained.

[0042] Using castor oil polyoxyethylene ether EL-10 or castor oil polyoxyethylene ether EL-80 to replace castor oil polyoxyethylene ether EL-40, using the above-mentioned ratio and method, can also prepare the cationic Dyes are easy to...

Embodiment 2

[0054] Cationic dye easy-to-dye copolyester fiber dyeing aid formula:

[0055] Dipropylene Glycol Dibenzoate 49%

[0056] Macrogol 600 35%

[0057] Pentaerythritol 5%

[0058] Octadecyltrimethylammonium Chloride 5%

[0059] Polyethylene glycol 400 monooleate 6%

[0060] Preparation method: Add octadecyltrimethylammonium chloride and polyethylene glycol 400 monooleate into a blender, heat while stirring, when the temperature rises to 50°C, add polyethylene glycol under slow stirring 600 and pentaerythritol, and then add dipropylene glycol dibenzoate under slow stirring to obtain a light yellow transparent liquid, which is cooled to room temperature while stirring to obtain a stable liquid. The cationic dye easy-to-dye copolyester fiber dyeing aid of the present invention can be obtained.

[0061] Cationic dye easy-to-dye copolyester fiber dyeing method:

[0062] Fiber for dyeing: polyol copolyester fiber yarn (Poliloff dyeable polyester)

[0063] Process formula:

[006...

Embodiment 3

[0071] Cationic dye easy-to-dye copolyester fiber dyeing aid formula:

[0072] Triethylene glycol dibenzoate 50%

[0073] Propylene Glycol 35%

[0074] Pentaerythritol 5%

[0075] Cetyltrimethylammonium Bromide 6%

[0076] Dodecylamine ethoxylate 4%

[0077] Preparation method: Add cetyltrimethylammonium bromide and laurylamine polyoxyethylene ether into a stirrer, heat while stirring, add propylene glycol and pentaerythritol under slow stirring when the temperature rises to 60°C, and stir evenly , and then added triethylene glycol dibenzoate under slow stirring to obtain a light yellow transparent liquid, which was lowered to room temperature while stirring to obtain a stable liquid. The cationic dye easy-to-dye copolyester fiber dyeing aid of the present invention can be obtained.

[0078] Cationic dye easy-to-dye copolyester fiber dyeing method:

[0079] Fiber for dyeing: polyol copolyester fiber (normal temperature dyeable polyester ECDP) 21 woven fabrics

[0080] P...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cationic chromophilous copolyester fibre dyeing assistant and a dyeing method using same. The copolyester fibre assistant comprises the following components by mass percentage: 45-57% of polyol benzoate, 35-45% of polyol, 4-10% of nonionic surfactant and 4-10% of cationic surfactant. The cationic dye chromophilous copolyester fibre dyeing assistant in the invention is a green and environment-friendly assistant, and has no odor and toxicity as well as low COD. The assistant can help the cationic chromophilous copolyester fibre to realize dyeing at a low temperature, the dyeing temperature can be lowered to 60 DEG C, and the dyeing effect is as good as that at the temperature of 98-100 DEG C, thus greatly lowering energy consumption.

Description

technical field [0001] The invention relates to a fiber dyeing aid and a dyeing method thereof, in particular to a cationic dye easy-to-dye copolyester fiber dyeing aid and a dyeing method thereof. Background technique [0002] Since the advent of chemical fibers, synthetic fibers, especially polyester fibers, have developed rapidly. The output of polyester fibers in my country ranks first in the world, and it is the textile fiber with the largest domestic production and consumption. With the advancement of industrial technology, people's demand for textile fibers has become wider and higher, and the required performance has become higher and higher. Countries have begun to develop a large number of differentiated fiber materials, and the proportion of differentiated fibers in synthetic fibers has increased rapidly. . Judging from the research and development of various countries, polyester fibers account for the largest proportion of differentiated fibers. [0003] Polyes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/60D06P1/651D06P1/66D06P3/52
Inventor 李颖君张庆李慧霞臧蕴王蓉姚晓静
Owner 嘉善嘉胜绢纺股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap