Deoxidizing preservative and preparation method thereof

A technology of deoxidizing preservatives and fillers, applied in food preservation, food science, application and other directions, can solve the problems of increasing the amount of deoxidizers, depleting oxygen absorption performance, increasing costs, etc., and reducing the loss of oxygen absorption performance and loss of oxygen absorption. Performance, low cost effect

Active Publication Date: 2010-12-08
GUANGDONG GUANGYI TECH IND
View PDF5 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] On the other hand, if the above ingredients are mixed and then packaged, the material will absorb oxygen in the environment during the process from mixing to packaging, thus greatly depleting the oxygen absorption performance, and sometimes, the oxygen absorption performance loss is close to 20%.
In order to ensure product performance, deoxidizer manufacturers have to increase the amount of deoxidizer, which increases the cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A deoxidation preservative, comprising oxygen absorbing body and water, by weight, the content of each component of the deoxidation preservative is

[0025] Oxygen Absorber 90%

[0026] water 10%

[0027] The oxygen-absorbing body is a block solid, which contains oxygen-absorbing substances, activated carbon and ultra-high molecular weight polyethylene. By weight, the content of each component in the oxygen-absorbing body is:

[0028] UHMWPE 90%;

[0029] Oxygen-absorbing substances 5%;

[0030] Activated carbon 5%;

[0031] Wherein, the molecular weight of the ultra-high molecular weight polyethylene is 2.5-3 million Daltons; the oxygen-absorbing substance is reduced iron powder; the particle diameters of the reduced iron powder and the activated carbon are both 50-150 microns.

[0032] The preparation method of above-mentioned deoxidation preservative comprises the steps:

[0033] Step A: Weigh 81g of ultra-high molecular weight polyethylene powder, 4.5g of reduc...

Embodiment 2

[0037] A deoxidation preservative, comprising oxygen absorbing body and water, by weight, the content of each component of the deoxidation preservative is

[0038] Oxygen Absorber 95%

[0039] water 5%

[0040] The oxygen-absorbing body is a block solid, which contains oxygen-absorbing material, activated carbon, ultra-high molecular weight polyethylene, filler, pore forming agent, catalyst and water-absorbing agent; by weight, the content of each component in the oxygen-absorbing body for:

[0041] UHMWPE 40%;

[0042] Oxygen-absorbing substances 15%;

[0043] Activated carbon 5%;

[0044] filler 10%;

[0045] Pore ​​forming agent 5%;

[0046] Catalyst 10%;

[0047] Water absorbent 15%;

[0048] Wherein, the molecular weight of the ultra-high molecular weight polyethylene is 3 to 4 million Daltons; the oxygen-absorbing substance is a mixture of zinc powder and ferrous chloride; the filler is silicon dioxide; the pore-forming agent is Sodium bicarbonate, the catalyst ...

Embodiment 3

[0054] A deoxidation preservative, comprising oxygen absorbing body and water, by weight, the content of each component of the deoxidation preservative is

[0055] Oxygen Absorber 85%

[0056] water 15%

[0057] The oxygen-absorbing body is a block solid, which contains oxygen-absorbing material, activated carbon, ultra-high molecular weight polyethylene, filler, pore forming agent, catalyst and water-absorbing agent; by weight, the content of each component in the oxygen-absorbing body for:

[0058] UHMWPE 50%;

[0059] Oxygen-absorbing substances 25%;

[0060] Activated carbon 8%;

[0061] filler 5%;

[0062] Pore ​​forming agent 2%;

[0063] Catalyst 5%;

[0064] Water absorbent 5%;

[0065] Wherein, the molecular weight of the ultra-high molecular weight polyethylene is 3 to 4 million Daltons; the oxygen-absorbing substance is a mixture of ferrous carbonate and ferrous chloride; the filler is vermiculite and diatomaceous earth; the hair The pore agent is sodium bica...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a deoxidizing preservative. The deoxidizing preservative comprises the following components in percentage by weight: 85 to 95 percent of oxygen absorbent and 5 to 15 percent of water; the oxygen absorbent is blocky solid and comprises the following components in percentage by weight: 40 to 90 percent of ultrahigh molecular weight polyethylene, 5 to 55 percent of oxygen absorbing substance and 5 to 20 percent of active carbon, wherein the oxygen absorbing substance is one or a mixture of reduced iron powder, ferrous chloride, ferrous carbonate, ferrous sulfate and zinc powder. The deoxidizing preservative not only prevents food pollution caused by powder leakage, but also prevents materials from adsorbing oxygen in the environment in the processes from mixing to packing so as to greatly lose oxygen absorption performance and reduce the production cost for manufacturers of the deoxidizing preservative.

Description

Technical field: [0001] The invention relates to the technical field of externally controlled fresh-keeping of food, in particular to a deoxidizing fresh-keeping agent and a preparation method thereof. Background technique: [0002] At present, the deoxidizing preservatives produced by most enterprises at home and abroad use reduced iron powder, activated carbon, water-absorbing agent or catalyst as the main components, and are packaged with perforated film, perforated composite film, and misplaced perforated film. Since these substances are all powdery substances, if the perforated film is used for packaging, the powdery substance is easy to leak from the film holes and cause powder leakage to contaminate food. Although the products packaged in perforated composite film and misplaced perforated film can avoid the phenomenon of powder leakage, due to the limitation of the production process, there are often false seals in the sealing area and insufficient temperature and pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A23L3/3436
Inventor 陈永恒扶承荣
Owner GUANGDONG GUANGYI TECH IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap