A preparation process, molybdenum powder technology, applied in the field of molybdenum billet preparation, can solve the problem that it is difficult to meet the number of grains for production

Inactive Publication Date: 2011-02-09
JINDUICHENG MOLYBDENUM CO LTD
View PDF1 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the particle size of molybdenum powder used in industry is generally between 2 and 5um, which is difficult to meet ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Fully mix 0.5-1um submicron molybdenum powder in a mixer for 5 hours, take 1000g of molybdenum powder and press it on a hydraulic press with a pressing pressure of 100MPa. The blank was fired in an intermediate frequency furnace at a sintering temperature of 500°C for 120min, 800°C for 120min, 1250°C for 120min, 1500°C for 120min, and 1700°C for 300min. The obtained molybdenum blank has a density of 9.95g / cm 3 , the number of grains is 10000 / mm 2 , the grain size is 700nm

Embodiment 2

[0014] Fully mix 0.5-1um submicron molybdenum powder in a mixer for 5 hours, take 1000g of molybdenum powder and press it on a hydraulic press with a pressing pressure of 100MPa. The blank was fired in an intermediate frequency furnace at a sintering temperature of 500°C for 120min, 800°C for 120min, 1250°C for 120min, 1500°C for 120min, and 1600°C for 120min. The obtained molybdenum blank has a density of 9.90g / cm 3 , the number of grains is 16000 / mm 2 , The grain size is 500nm.

Embodiment 3

[0016] Fully mix 0.5-1um submicron molybdenum powder in a mixer for 5 hours, take 1000 grams of molybdenum powder and press it into a molybdenum rod on an isostatic press with a pressing pressure of 120MPa. The blank was fired in an intermediate frequency furnace at a sintering temperature of 500°C for 120min, 800°C for 120min, 1250°C for 120min, 1500°C for 120min, and 1700°C for 240min. The obtained molybdenum blank has a density of 9.96g / cm 3 , the number of grains is 12000 / mm 2 , The grain size is 680nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Densityaaaaaaaaaa
Grain sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a molybdenum blank preparing method, and relates to a method for preparing a pure molybdenum blank with the grain number of 5,000 to 20,000/mm<2> and the grain size of 300 to 800nm. The molybdenum blank preparing method is characterized in that: in the preparation process, submicron-scale molybdenum powder with the granularity of 0.5 to 1um is taken as a raw material and is pretreated, molded and sintered into a molybdenum blank. In the molybdenum blank preparing method, the molybdenum powder is taken as a raw material, and the molybdenum blank with fine grains can be prepared by reducing sintering temperature and shortening the sintering time, and has the density of 9.8 to 10.0, the grain number of 5,000 to 20,000/mm<2> and the grain size of 300 to 800nm. The submicron-scale molybdenum powder is taken as the raw material for preparing the molybdenum blank with fine grains, special requirements on production equipment are absent, and the method is suitable for industrial production.

Description

technical field [0001] A method for preparing molybdenum blanks, involving a crystal grain number of 5000-20000 / mm 2 1. A method for preparing pure molybdenum blanks with a grain size of 300-800nm. Background technique [0002] The preparation method of molybdenum billet usually adopts the method of powder metallurgy, the preparation process uses molybdenum powder as raw material, after pretreatment, molding, sintering to make molybdenum billet. The particle size and distribution of molybdenum powder have a great influence on the density and grain size of sintered products. At present, the particle size of molybdenum powder used in industry is generally between 2 and 5um, which is difficult to meet the production requirements and the number of grains can reach 5,000 to 20,000 / mm 2 , Molybdenum blanks with a grain size of 300-800nm ​​are required. Contents of the invention [0003] The purpose of the present invention is to provide a method for preparing crystal grains w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F3/16
Inventor 唐丽霞黄晓玲薛夏英郭军刚卜春阳崔玉清
Owner JINDUICHENG MOLYBDENUM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap