System for testing damage to gradient composite under thermal/electric/magnetic/coupling action

A gradient material and testing system technology, applied in the direction of analyzing materials, measuring devices, strength characteristics, etc., can solve the problems that the testing of gradient material mechanics and electromagnetic performance indicators cannot be carried out

Inactive Publication Date: 2011-02-23
BEIJING INSTITUTE OF TECHNOLOGYGY
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If such problems cannot be solved, it will make it impossible to test the m

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • System for testing damage to gradient composite under thermal/electric/magnetic/coupling action
  • System for testing damage to gradient composite under thermal/electric/magnetic/coupling action
  • System for testing damage to gradient composite under thermal/electric/magnetic/coupling action

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Implementation mode: The electromagnetic principle diagram of the test system of the present invention is as follows figure 1 Shown. A gradient layer with a thickness of 121 μm was prepared on the metal substrate by the self-propagating combustion synthesis method and cut into a gradient material sample with a width of 20 μm and a length of 69 μm. Such as figure 2 As shown, the sensor probe is fixed on the fixture, the displacement of the fixture is controlled so that the sensor probe contacts the gradient material, and then the current density applied to the gradient material is 82mA / cm 2 . Actually build as figure 2 As shown, due to the alternating thermal stress generated by the direct current in the gradient material, the gradient material passes through 7.58×10 5 Seconds later, holes, microcracks and damage were generated, and further direct current was applied until failure and destruction occurred.

[0019] During the whole test process, the CCD probe of the sca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the establishment of a system for testing and evaluating damage to a gradient composite under a thermal/electric/magnetic/coupling action and a performance test method. The mechanical property and the physical property of a gradient material are tested by a direct current under the thermal/electric/magnetic/coupling action. The damage to the gradient composite is tested and evaluated by thermal impacting stress generated due to the joule heat caused by the direct current and the thermal expansion coefficient difference of a ceramic and metal gradient composite. The system established in the invention combines damage and property test and characterization integrally and can test the physical and mechanical coupling properties of the gradient material.

Description

technical field [0001] The invention relates to the establishment of a damage test system and a damage performance test method of a gradient composite material under the action of thermodynamic and electromagnetic coupling, and belongs to the technical field of coupling analysis of mechanical experiments and physical properties. Background technique [0002] Gradient composite materials are widely used in thermal protection, electromagnetic protection and other fields. Due to the long-term work under the condition of thermodynamic and electromagnetic coupling, and the gradient material is composed of different materials, the difference in thermal expansion coefficient of the material will cause thermal stress inside the material, which will affect its mechanical reliability and cause mechanical damage. Therefore, it is of great theoretical significance and application value to test the actual working conditions of the gradient material after passing the current to correctly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N3/02G01N3/60
Inventor 李永舒畅
Owner BEIJING INSTITUTE OF TECHNOLOGYGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap