Continuous casting method for steel billets

A continuous casting and billet technology, applied in the field of billet continuous casting, can solve problems such as cold steel, poor welding of old and new molten steel, and steel breakout accidents, and achieve the effect of eliminating steel breakout accidents.

Inactive Publication Date: 2011-05-18
PANGANG GROUP VANADIUM TITANIUM & RESOURCES +1
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Through long-term production practice, it is found that in the above-mentioned billet continuous casting process, cold steel is prone to appear on the surface of the molten steel in the crystallizer, which will lead to poor welding of the old and new molten steel at the seam when the tundish is replaced, which will easily cause leakage. steel accident

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The following examples are used to illustrate the method for continuous casting of steel slabs provided by the present invention.

[0024] The molten steel of the composition described in Table 1 is injected into the crystallizer for continuous casting, and mold powder is added to the mold at the same time, and the mold powder contains 35.5% by weight of CaO and 34.5% by weight of SiO 2 , 6.5 wt% Al 2 o 3 , 6.7 wt% Na 2 O, 4.8% by weight of C, the rest being Fe 2 o 3and MnO, with respect to each ton of the molten steel, the addition of mold slag in the mold is 0.5 kilograms, so that the mold slag in the mold has a thickness of 15 mm from top to bottom. 10mm layer of sintered slag and 10mm thick layer of liquid slag. The continuous casting conditions include: the casting speed is 1 m / min, and the cross-sectional size of the slab is 200mm×1160mm. 8 minutes before the injection of molten steel into the crystallizer at the end of the tundish, by reducing the addition ...

Embodiment 2

[0027] The following examples are used to illustrate the method for continuous casting of steel slabs provided by the present invention.

[0028] The molten steel of the composition described in Table 1 is injected into the crystallizer for continuous casting, and mold powder is added to the mold at the same time, and the mold powder contains 35.5% by weight of CaO and 34.5% by weight of SiO 2 , 6.5 wt% Al 2 o 3 , 6.7 wt% Na 2 O, 4.8% by weight of C, the rest being Fe 2 o 3 and MnO, with respect to each ton of the molten steel, the addition of the mold slag in the mold is 0.55 kilograms, so that the mold slag in the mold has a thickness of 18 mm from top to bottom. 12mm sintered slag layer and 13mm liquid slag layer. The continuous casting conditions include: the casting speed is 1 m / min, and the cross-sectional size of the slab is 200mm×1160mm. 5 minutes before the injection of molten steel into the crystallizer at the end of the tundish, by reducing the amount of mold ...

Embodiment 3

[0031] The following examples are used to illustrate the method for continuous casting of steel slabs provided by the present invention.

[0032] The molten steel of the composition described in Table 1 is injected into the crystallizer for continuous casting, and mold powder is added to the mold at the same time, and the mold powder contains 35.5% by weight of CaO and 34.5% by weight of SiO 2 , 6.5 wt% Al 2 o 3 , 6.7 wt% Na 2 O, 4.8% by weight of C, the rest being Fe 2 o 3 and MnO, with respect to each ton of the molten steel, the addition of the mold slag in the mold is 0.6 kilograms, so that the mold slag in the mold has a thickness of 20 mm from top to bottom. 15mm layer of sintered slag and 16mm thick layer of liquid slag. The continuous casting conditions include: the casting speed is 1 m / min, and the cross-sectional size of the slab is 200mm×1160mm. 7 minutes before the injection of molten steel into the crystallizer at the end of the tundish, by reducing the amou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a continuous casting method for steel billets, which comprises the following steps of: injecting molten steel in a plurality of tundishes into a crystallizer in turn, performing continuous casting, and adding crystallizer slag powder into the crystallizer, wherein for each tundish, the addition amount of the crystallizer slag powder ensures that three layers of crystallizer slag powder, namely a raw slag layer, a sintering slag layer and a liquid slag layer, are formed in the crystallizer in turn from top to bottom in a first time period; and the addition amount of the crystallizer slag powder ensures that the sintering slag layer and the liquid slag layer are formed in the crystallizer in turn from top to bottom, or only the liquid slag layer is formed in a second time period, and the thickness of the sintering slag layer is less than 5mm. The continuous casting method for the steel billets can ensure that cold steel is not crystallized on the surface of the molten steel in the crystallizer, and new molten steel and old molten steel are well welded on a weld line when the tundishes are changed, and effectively avoids steel leakage accidents.

Description

technical field [0001] The invention relates to a method for continuous casting of steel slabs. Background technique [0002] Billet continuous casting is to use a tundish with a certain capacity to store molten steel to realize continuous casting of molten steel, that is, the molten steel in the molten steel tank reaches the tundish through the long nozzle, and the molten steel in the tundish reaches the crystallizer through the submerged nozzle. The molten steel is cooled by the cooling water around the crystallizer to form a solidified slab shell with a certain strength, which is continuously pulled out under the traction of the power system of the casting machine. [0003] The working layer of the tundish is knotted with refractory materials. It is in contact with molten steel during the casting process and is gradually eroded. After the erosion reaches a certain level, the safety of the casting process cannot be guaranteed. Therefore, the tundish must be replaced. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22D11/04B22D11/111
Inventor 周明佳
Owner PANGANG GROUP VANADIUM TITANIUM & RESOURCES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com