Novel wooden door coating method

A coating method and wooden door technology, applied in the direction of surface coating liquid device, coating, pretreatment surface, etc., can solve the problems of large VOC, large production site, low hardness, etc., to save production site and improve productivity And market competitiveness, the effect of high surface hardness

Inactive Publication Date: 2011-06-22
上海展辰涂料有限公司
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional wooden door primer coating is mainly based on polyurethane coating (PU), which generally has problems such as large VOC, thin coating, low hardness, low efficiency, and large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1

[0021] (1) Polish oak or Fraxinus mandshurica board with 600# sandpaper to remove dust;

[0022] (2) Spray UV vacuum spray primer with vacuum sprayer, coating amount: 100~120g / m 2 , (Commercial products can be used, such as Shanghai Fuchen Chemical UV vacuum spray primer VU2110B), after 50℃ infrared leveling for 2 to 3 minutes, adjust the UV lamp energy to 240mj / cm 2 , Fully cured by UV lamp;

[0023] (3) After sanding and leveling the primer with 320# sandpaper, add appropriate amount of color essence to perform PU color repair according to the coloring requirements (commercial products can be used, such as Shanghai Fuchen Chemical PU color repair topcoat V500);

[0024] (4) After the PU color repairing paint is dry for 1 hour, lightly polish the color repairing layer with 1000# sandpaper, and spray the PU paint (25℃, construction viscosity: Iwata No. 2 cup 12~13S) for one and a half degrees. Commercial products can be used, such as Shanghai Fuchen Chemical PU seve...

Example Embodiment

[0032] Implementation case 2

[0033] (1) Polish oak or Fraxinus mandshurica board with 600# sandpaper to remove dust;

[0034] (2) Spray UV vacuum spray primer with vacuum sprayer, coating amount: 60~80g / m 2 , (Commercial products can be used, such as Shanghai Fuchen Chemical UV vacuum spray primer VU2110B), after 50℃ infrared leveling for 2 to 3 minutes, adjust the UV lamp energy to 120mj / cm 2 , Semi-cured by UV lamp; spray UV vacuum spray primer with vacuum sprayer, coating amount: 60~80g / m 2 , (Commercial products can be used, such as Shanghai Fuchen Chemical UV vacuum spray primer VU2110B), after 50℃ infrared leveling for 2 to 3 minutes, adjust the UV lamp energy to 250mj / cm 2 , UV lamp is fully cured; after the primer is sanded and leveled with 320# sandpaper, spray UV vacuum spray primer with a vacuum sprayer, coating amount: 100~120g / m 2 , (Commercial products can be used, such as Shanghai Fuchen Chemical UV vacuum spray primer VU2110B), after 50℃ infrared leveling for 2 to 3...

Example Embodiment

[0043] Example 3

[0044] (1) Polish the cherry wood or Sapele board with 600# sandpaper to remove the dust;

[0045] (2) Spray UV vacuum spray primer with vacuum sprayer, coating amount: 80~100g / m 2 , (Commercial products can be used, such as Shanghai Fuchen Chemical UV vacuum spray primer VU2110B), after 50℃ infrared leveling for 2 to 3 minutes, adjust the UV lamp energy to 250mj / cm 2 , UV lamp is fully cured; after the primer is sanded and leveled with 320# sandpaper, spray UV vacuum spray primer with a vacuum sprayer, coating amount: 100~120g / m 2 , (Commercial products can be used, such as Shanghai Fuchen Chemical UV vacuum spray primer VU2110B), after 50℃ infrared leveling for 2 to 3 minutes, adjust the UV lamp energy to 240mj / cm 2 , Fully cured by UV lamp.

[0046] (3) After sanding and leveling the primer with 320# sandpaper, add appropriate amount of color essence to perform PU color repair according to the coloring requirements (commercial products can be used, such as Shangh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a novel wooden door coating method which comprises the following steps of: 1, carrying out sand papering on a base material, and removing dust; 2, performing priming paint spraying in vacuum by using UV, and curing with UV-light, wherein the times of the performing is determined according to the coating requirement; 3, after the priming paint is sanded with the UV, spraying PU (polyurethane) padding finish paint; and 4, after light sanding, spraying a PU surface, and completely drying to obtain a finished product. The novel wooden door coating method provided by the invention has the advantages of having no VOC emission when the priming paint is sprayed for coating in vacuum by using the UV, improving the board hardness, greatly increasing the productivity and the market competitiveness, and saving the production space at the same time.

Description

technical field [0001] The invention relates to a new coating method for wooden doors. Background technique [0002] With the improvement of people's living standards, the replacement of wooden doors is getting faster and faster, and the market demand is increasing day by day. The traditional wooden door primer coating is mainly based on polyurethane coating (PU), which generally has problems such as large VOC, thin coating, low hardness, low efficiency, and large production site. Therefore, the furniture industry urgently needs a new process to replace the existing one. Production mode to meet the production needs of large-scale efficiency improvement. Contents of the invention [0003] The purpose of the present invention is to overcome above-mentioned defect, a kind of new wooden door coating method is provided. [0004] The method of the present invention comprises the steps of: [0005] (1) Grinding the substrate with 240# sandpaper to remove dust; [0006] (2) Co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B05D7/08B05D3/12B05D3/06
Inventor 王向科邓静
Owner 上海展辰涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap