Hydrogel forming covalent cross-linking rapidly under mild conditions and preparation method thereof

A hydrogel and component technology, used in prostheses, bandages, surgery, etc., can solve the problems of slow hydrogels, unsuitable surgical sealants, and difficult to control the actual operation of hydrogel systems, achieving excellent viscoelasticity, The effect of structural stabilization

Active Publication Date: 2011-10-05
HAINAN JIANKE PHARMA
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This FocalSeal as a surgical sealant ? The disadvantage of the hydrogel system is that it is somewhat difficult to control in practice
However, since the two solutions disclosed in WO2008 / 131325 are mixed to form a hydrogel slowly (about 3 minutes), it is not suitable as a surgical sealant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrogel forming covalent cross-linking rapidly under mild conditions and preparation method thereof
  • Hydrogel forming covalent cross-linking rapidly under mild conditions and preparation method thereof
  • Hydrogel forming covalent cross-linking rapidly under mild conditions and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0044] The preparation method of above-mentioned hydrogel comprises the following steps:

[0045] 1) Dissolve components A and B in a solution with a pH of 7 to 8 to obtain a mixed solution of components A and B respectively;

[0046] 2) Mix the mixed solutions of components A and B to obtain a hydrogel.

[0047] Preferably, the mass volume concentration of the mixed solution of components A and B is 5%-20%.

[0048] Preferably, components A and B are mixed in a molar ratio of 4:1 to 1:4.

[0049] Preferably, the solution with a pH of 7-8 is a sodium phosphate buffer. Of course, other buffers can also be used.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hydrogel forming covalent cross-linking rapidly under mild conditions and a preparation method thereof. The hydrogel contains two components, i.e. NHS (N-Hydroxy Succinimide) ester of PEG (Polyethylene Glycol) and PEG containing N-terminal group cysteine. The two components are dissolved and mixed to obtain the hydrogel. The hydrogel disclosed by the invention can form covalent cross-linking rapidly under mild conditions, and is particularly suitable for being manufactured into surgical sealants.

Description

technical field [0001] The invention relates to a hydrogel and a preparation method thereof, in particular to a hydrogel capable of rapidly forming covalent crosslinks under mild conditions and a preparation method thereof. Background technique [0002] Hydrogel (Hydrogel) is a hydrophilic polymer network structure, insoluble in water, but can absorb and retain a large amount of water, highly swellable in aqueous solution, and has good biocompatibility and similarity. They can be used in surgical sealants and adhesives, drug release, tissue repair and tissue engineering in the field of medicine and biology. [0003] Existing hydrogel systems are usually formed through chemical or physical actions. Chemical crosslinking to form aqueous gels often involves the use of toxic crosslinking agents and free radicals, and the resulting hydrogels are usually not biodegradable. On the other hand, physical hydrogels are formed through non-covalent interactions, such as hydrogen bonds,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61L15/26C08L71/08C08J3/24C08G81/00A61L24/04A61L15/42C08G65/48C08J3/075
CPCC08G65/3356C08J3/246A61L27/18C08J3/075C08J2371/08C08G65/33341A61L24/04C08L71/08C08L71/02A61L15/42C08G65/48C08J3/24A61L15/26C08G65/33337C08J2371/02C08G81/00
Inventor 胡碧煌胡晓阳胡天柱
Owner HAINAN JIANKE PHARMA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com