An imitation electroplating and coating technology, applied in the field of imitation electroplating coatings, can solve the problems of erosiveness that cannot reach the main engine factory, blackened coating film, and inapplicability, etc., and achieve the effect of good brightness, strong metallic feeling and stable properties
Active Publication Date: 2012-07-25
广东四方威凯高新技术有限公司
View PDF1 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, the current popular imitation electroplating coatings in the market cannot meet the technical requirements of OEMs in terms of water resistance, acid and alkali resistance and other media erosion. After trial, the coating film will be partially blackened or even peeled off. , Toyota and other products for application
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0025] Imitation electroplating paint, made of
[0026]
[0027] composition.
Embodiment 2
[0029] Imitation electroplating paint, made of
[0030]
[0031] composition.
Embodiment 3
[0033] Imitation electroplating paint, made of
[0034]
[0035] composition.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses an imitated plating coating, which consists of silicon dioxide coated imitated plating aluminum paste, polyurethane elastomer, closed isocyanate polymer, trimethoxy silane with epoxy group, triethoxysilane with epoxy group, polyether modified polydimethylsiloxane and solvent. The imitated plating coating has no toxicity or harm, has strong metal feeling, good brightness and good adhesive force after film formation, has excellent imitated plating effect, particularly good chemical resistance and stable property, and can well replace a plating process.
Description
technical field [0001] The invention relates to a paint, in particular to an imitation electroplating paint with outstanding chemical resistance. Background technique [0002] In the surface treatment industry, electroplating is one of the processes that cause the most serious environmental pollution. It is mainly a series of waste liquids produced by surface treatment processes such as electroplating, which contain harmful heavy metals, and the environmental protection treatment of waste liquids is difficult. The discharge of waste water that does not meet the standards has caused great pollution to the environment and brought great risks to human health. Therefore, the electroplating process is facing elimination, and the birth and application of energy-saving and environmentally-friendly products with similar effects has become an inevitable . [0003] As a result, a coating that can achieve the effect of electroplating quietly emerged in the market and quickly occupied ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D7/12C09D5/00
Inventor 方芳朱洪江
Owner 广东四方威凯高新技术有限公司