Sky blue-imitated nanometer paint for anticorrosion and organic pollutant decomposition

A technology of organic pollutants and nano-coatings, applied in the direction of anti-corrosion coatings, polyamide coatings, coatings, etc., can solve the problem that the decontamination performance of coatings is lower than the optimal level

Inactive Publication Date: 2014-05-28
ANHUI MEIJIA NEW MATERIAL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the stain release performance of the paint is less than optimal in low light conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sky blue-imitated nanometer paint for anticorrosion and organic pollutant decomposition
  • Sky blue-imitated nanometer paint for anticorrosion and organic pollutant decomposition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The weight parts of the paint are as follows:

[0023] Flake aluminum powder 1

[0024] Phthalocyanine blue 2

[0025] Anatase nano titanium dioxide with a particle size of 30nm 14

[0026] Translucent spherical blue pigment with a particle size of 90nm 40

[0027] Large white powder with a particle size of 100nm 2

[0028] Polyamide modified alkyl resin with 20% mineral oil gel 30

[0029] Solvent 10

[0030] Anti-skinning agent 0.15

[0031] 25% solid content cobalt naphthenate desiccant 0.85.

[0032] Compared with conventional coatings, the technical effects of the embodiments of the present invention are as follows:

[0033]

[0034] The paint of the present invention has outstanding anti-corrosion performance, and at the same time has an ecological environment-friendly color and the function of decomposing organic pollutants. The multi-component achieves a synergistic effect, which is greater than any single component. A vast space for more practical applications.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a sky blue-imitated nanometer paint for anticorrosion and organic pollutant decomposition. The paint comprises the following components: 1 part of laminar aluminum powder, 2 parts of phthalocyanine blue, 14 parts of anatase nanometer titanium dioxide, 40 parts of a semitransparent spherical blue pigment with the particle size of 90nm, 2 parts of calcium carbonate with the particle size of 100nm, 30 parts of an alkyl resin modified with polyamide containing 20% of mineral oil gel, 10 parts of a solvent, 0.15 parts of an antiskinning agent, and 0.85 parts of a drying agent cobaltous naphthenate with the solid content of 25%. The paint of the present invention which provides a visual relax for humans allows efficacies of anticorrosion and organic pollutant decomposition to be simultaneously reached.

Description

Technical field [0001] The invention relates to a paint, especially a nano paint which imitates the sky blue anticorrosion and decomposes organic pollutants. Background technique [0002] With the development of the national economy and high technology, in addition to general-purpose coatings, the demand for special coatings is increasingly urgent. In anticorrosive coatings, peroxyethylene coatings, epoxy resin coatings, and oxysulfonated polyethylene coatings all exist together, but each has its own shortcomings. Peroxyethylene paint came out in the early 1970s. This type of paint has a certain anti-corrosion effect, but due to its larger molecular weight, the leveling performance is not ideal, the solid content is low, generally only 14-18%, the film density is poor, and the viscosity is also very high. Low, only 20-50 seconds, its adhesion is not good, and the paint film is easy to fall off. [0003] Epoxy resin coatings have been used since the early 1960s and have been used ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/10C09D7/12C09D177/00
Inventor 王方银王峰
Owner ANHUI MEIJIA NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com