Environmentally-friendly dope for solidifying direct-vacuum aluminized paper by electron beam and preparation method thereof

A technology of electron beam curing and vacuum aluminized paper, applied in paper coating, papermaking, coating, etc., can solve the problems of poor coating leveling, easy cracking of coating, insufficient toughness, etc., and achieve good temperature resistance and bending Good anti-burst performance and good wear resistance

Active Publication Date: 2014-01-01
HONGYUN HONGHE TOBACCO (GRP) CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there are still two urgent problems to be solved in the curing of epoxy resin by cationic mechanism: one is that the viscosity of the solvent-free epoxy resin system is relatively high, resulting in poor leveling of the coating; the other is that bisphenol A epoxy resin is cured by electron beams. Insufficient post toughness, the coating is easy to burst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmentally-friendly dope for solidifying direct-vacuum aluminized paper by electron beam and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Put 20g of octyl glycidyl ether into the equipped three-necked bottle, start stirring and raise the temperature to 50℃~60℃, add 5g novolac epoxy resin F-51 and 75g epoxy resin E-51 in sequence, stir for 30min, then add 3g of initiator diphenyliodonium hexafluorophosphate, stirred evenly, filtered, and discharged to obtain an environmentally friendly electron beam curing coating for direct vacuum aluminized paper.

Embodiment 2～5

[0024] The preparation process is the same as in Example 1, and the specific formula is shown in Table 1.

[0025] Table 1

[0026]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
thermal resistanceaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environmentally-friendly dope for solidifying direct-vacuum aluminized paper by an electron beam and a preparation method thereof. The preparation method comprises the following steps of: weighing 10-90 parts of epoxy resin, 5-30 parts of epoxy active diluents, 2-5 parts of initiators; agitating the epoxy active diluents and raising the temperature to 50-60 DEG C; adding the epoxy resin, agitating for 30 min; adding the initiators, filtering after uniform agitating and obtaining the required environmentally-friendly dope for solidifying the direct-vacuum aluminized paper by the electron beam. The dope has moderate viscosity and can be applied to prime coat and surface coating processes of the direct-vacuum aluminized paper; and compared with a dope layer of a traditional dope, a dope layer solidified by the electron beam is more greatly improved in temperature tolerance and flexibility, and the anti-burst performance during the bending of the direct-vacuum aluminized paper is improved.

Description

technical field [0001] The invention belongs to the technical field of radiation curing coatings, in particular to an environment-friendly electron beam curing coating for direct vacuum aluminized paper. At the same time, the invention also relates to a preparation method of the paint. Background technique [0002] Cigarette rod and box wrapping paper and cigarette inner lining paper are extremely important packaging materials for cigarettes. The vacuum aluminum plating technology used in domestic cigarette materials is divided into two types according to the production process (transfer method) and (direct plating method). That is what people often say transfer paper and direct plating paper. In the production process of the transfer method, PET or BOPP film needs to be used as a carrier, vacuum aluminum-plated on the film and then transferred and compounded with paper, and the film is peeled off after long-term curing. It inevitably uses a large amount of volatile solven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H19/00D21H19/24D21H19/62
Inventor 曾哓鹰詹建波者为李庚余振华范多青张天栋
Owner HONGYUN HONGHE TOBACCO (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com