Environmentally-friendly size composition for tyre surface of tyre and preparation method thereof

A tire tread and environmental protection technology, applied in the direction of special tires, tire parts, rolling resistance optimization, etc., can solve the problems that tire performance cannot be guaranteed, tires cannot meet environmental protection requirements, etc., so as to reduce hidden dangers of pollution, improve competitiveness and value, good tearing strength effect

Active Publication Date: 2012-04-11
SICHUAN YUANXING RUBBER
View PDF3 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

People pay more and more attention to the coexistence of tire environmental protection and performance, but there are generally two situations in terms of the current tire form: one is that the performance of the tire can meet the national standard and the needs of consumers, but the tire cannot meet the environmental protection requirements of the European Union; two. It is the tire that can meet the requirements of environmental protection, but the performance of the tire cannot be guaranteed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The weight ratio of each component raw material is:

[0029] Natural rubber 1# standard rubber: 40 copies;

[0030] SBR 1502E: 35 parts;

[0031] Butadiene rubber BR9000: 25 parts;

[0032] Carbon black N330: 35 parts;

[0033] Carbon black N660: 10 parts;

[0034] Environmental protection aromatic oil: 5 parts;

[0035] Hydrocarbon resin (C5 resin): 1 part;

[0036] Zinc oxide: 3.5 parts;

[0037] Stearic acid: 0.5 parts;

[0038] Anti-aging agent 4020: 0.5 parts;

[0039] Protective wax: 1 part;

[0040] Accelerator NS: 0.1 part;

[0041] Homogenizer A78: 0.5 parts;

[0042] Insoluble sulfur: 1 part;

[0043] The tear strength, tensile strength and hardness of the above compounds have been improved. The tear strength is about 50% higher than that of ordinary tires, the tensile strength is 15% higher than that of ordinary tires, and the hardness is 6 %.

Embodiment 2

[0045] The weight ratio of each component raw material is:

[0046] Natural rubber 1# standard rubber: 50 copies;

[0047] SBR 1502E: 30 parts;

[0048] Butadiene rubber BR9000: 20 parts;

[0049] Carbon black N330: 40 parts;

[0050] Carbon black N660: 15 parts;

[0051] Environmental protection aromatic oil: 10 parts;

[0052] Hydrocarbon resin (C5 resin): 1.5 parts;

[0053] Zinc oxide: 4 parts;

[0054] Stearic acid: 1 part;

[0055] Anti-aging agent RD: 1 part;

[0056] Anti-aging agent 4020: 1 part;

[0057] Protective wax: 1.5 parts;

[0058] Accelerator NS; 0.3 parts;

[0059] Homogen A78: 1 part;

[0060] Insoluble sulfur: 2.5 parts.

[0061] The tear strength, tensile strength and hardness of the above compounds have been improved. The tear strength can be increased by about 52% compared with ordinary tires, the tensile strength is 18% higher than that of ordinary tires, and the hardness is higher than that of ordinary tires. Up 5%.

Embodiment 3

[0063] The weight ratio of each component raw material is:

[0064] Natural rubber 1# standard rubber: 60 copies;

[0065] SBR 1502E: 25 parts;

[0066] Butadiene rubber BR9000: 15 parts;

[0067] Carbon black N330: 45 parts;

[0068] Carbon black N660: 20 parts;

[0069] Environmental protection aromatic oil: 15 parts;

[0070] Hydrocarbon resin (C5 resin): 3 parts;

[0071] Zinc oxide: 4.5 parts;

[0072] Stearic acid: 1.5 parts;

[0073] Anti-aging agent 4020; 1.5 parts;

[0074] Anti-aging agent RD: 1.5 parts;

[0075] Protective wax: 3 parts;

[0076] Accelerator NS: 0.6 parts;

[0077] Homogenizer A78: 1.5 parts;

[0078] Insoluble sulfur: 4 parts.

[0079] The tear strength and tensile strength of the environmentally-friendly rubber compound are improved, the tear strength can be increased by about 55% compared with the rubber compound of ordinary tires, and the tensile strength is 20% higher than that of ordinary tires.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environmentally-friendly size composition for a tyre surface of a tyre and a preparation method thereof. The environmentally-friendly size composition comprises natural rubber, butadiene styrene rubber, butadiene rubber, carbon black, zinc oxide, stearic acid, an antiager, C5 resin, insoluble sulfur, environmentally-friendly arene oil, an accelerator and a homogenizing agent and various other components. The environmentally-friendly size can be prepared by the steps of plastifying and mixing the raw materials and the like. The environmentally-friendly size composition for the tyre surface of a tyre and size obtained by using the preparation method have better breaking strength, tensile strength and hardness, meet environmentally-friendly requirement and are prepared from environmentally-friendly raw materials which do not contain harmful substances, wherein arene oil, C5 resin, insoluble sulfur, carbon black and the like belong to the environmentally-friendly materials; and through adopting the environmentally-friendly raw materials coordinated with reasonable composition design, the environment pollution hidden danger caused in the production and use processes is greatly reduced, and the product has wider safety, economy and adaptability.

Description

Technical field [0001] The invention belongs to a tire tread rubber compound and a preparation method thereof, and particularly relates to an environmentally friendly tire tread rubber compound and a preparation method thereof. Background technique [0002] The tire is made up of a variety of materials. A common tire uses more than 20 materials, most of which are petroleum products. The European Union officially implemented the RoHS directive on July 1, 2006, and on January 1, 2010. The REACH regulations are formally implemented, both of which stipulate that tires must not contain substances harmful to the environment. With the rapid development of social economy today, environmental protection has received more and more attention, and environmentally friendly tires have also become the development trend of the tire industry. People are paying more and more attention to the coexistence of environmental protection and performance of tires, but in terms of current tire types, ther...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/00C08L9/06C08L9/00C08L57/02C08K13/02C08K3/04C08K3/22C08K3/06C08K5/01B60C1/00
CPCY02T10/862
Inventor 郑昌福李德见骆阳
Owner SICHUAN YUANXING RUBBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com