Scarlet glaze material for ceramics and preparation method thereof

A bright red and glaze technology, applied in the field of ceramic glaze production, can solve problems such as less success, and achieve the effects of improving yield, good gloss and pure color.

Active Publication Date: 2013-07-03
CHAOZHOU QINGFA CERAMICS
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Over the years, Chinese and foreign ceramic experts have invested a lot of manpower, material resources and financial resources, trying to fire the bright red porcelain that people dream of, but the success is relatively small. A major technological challenge ahead

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of scarlet glaze for ceramics and preparation method thereof:

[0016] 30 parts of potassium feldspar, 20 parts of quartz, 5 parts of marble, 8 parts of kaolin, 6 parts of transparent frit, 0.1 part of cadmium carbonate, 4 parts of bright red material, 50 parts of water;

[0017] (1) Mix 30 parts of potassium feldspar, 20 parts of quartz, 5 parts of marble, 8 parts of kaolin, 6 parts of transparent frit, and 50 parts of water evenly, ball mill for 15 hours, and the fineness reaches 325 mesh, and the obtained glaze is used for later use;

[0018] (2) Mix 0.1 part of cadmium carbonate and 4 parts of bright red material evenly, ball mill until the fineness reaches 325 mesh, and set aside;

[0019] (3) Mix the materials obtained in step (1) and step (2) evenly to obtain the scarlet glaze for ceramics.

Embodiment 2

[0021] A kind of scarlet glaze for ceramics and preparation method thereof:

[0022] 40 parts of potassium feldspar, 32 parts of quartz, 10 parts of marble, 12 parts of kaolin, 6 parts of transparent frit, 0.5 parts of cadmium carbonate, 5 parts of bright red material, 60 parts of water;

[0023] (1) Mix 40 parts of potassium feldspar, 32 parts of quartz, 10 parts of marble, 12 parts of kaolin, 6 parts of transparent frit, and 60 parts of water evenly, ball mill for 17 hours, and the fineness reaches 325 mesh, and the obtained glaze is used for later use;

[0024] (2) Mix 0.5 parts of cadmium carbonate and 8 parts of bright red material evenly, ball mill until the fineness reaches 325 mesh, and set aside;

[0025] (3) Mix the materials obtained in step (1) and step (2) evenly to obtain the scarlet glaze for ceramics.

Embodiment 3

[0027] A kind of scarlet glaze for ceramics and preparation method thereof:

[0028] 35 parts of potassium feldspar, 25 parts of quartz, 8 parts of marble, 10 parts of kaolin, 9 parts of transparent frit, 0.3 parts of cadmium carbonate, 8 parts of bright red material, 55 parts of water;

[0029] (1) Mix 35 parts of potassium feldspar, 25 parts of quartz, 8 parts of marble, 10 parts of kaolin, 9 parts of transparent frit, and 55 parts of water evenly, ball mill for 16 hours, and the fineness reaches 325 mesh, and the obtained glaze is used for later use;

[0030] (2) Mix 0.4 parts of cadmium carbonate and 8 parts of bright red material evenly, ball mill until the fineness reaches 325 mesh, and set aside;

[0031] (3) Mix the materials obtained in step (1) and step (2) evenly to obtain the scarlet glaze for ceramics.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a scarlet glaze material for ceramics, which is prepared from 30-50 parts of potash feldspar, 20-40 parts of quartz, 5-15 parts of marble, 8-15 parts of kaolin, 6-10 parts of clear frit, 0.1-0.5 part of cadmium carbonate, 4-12 parts of scarlet pigment and 50-70 parts of water. The preparation method comprises the following steps: evenly mixing the 30-50 parts of potash feldspar, 20-40 parts of quartz, 5-15 parts of marble, 8-15 parts of kaolin, 6-10 parts of clear frit and 50-70 parts of water, and carrying out ball milling for 15-20 hours until the fineness reaches 325 meshes; evenly mixing the 0.1-0.5 part of cadmium carbonate and 4-12 parts of scarlet pigment, and carrying out ball milling until the fineness reaches 325 meshes; and finally, evenly mixing the two mixtures to obtain the scarlet glaze material for ceramics. The glaze material has the advantages of favorable combination performance with the green body, pure and bright color, high stability and high gloss.

Description

technical field [0001] The invention relates to a red glaze and a preparation method thereof, in particular to a scarlet glaze for ceramics and a preparation method thereof, belonging to the technical field of ceramic glaze production. Background technique [0002] Red in Chinese red porcelain means peace, auspiciousness, jubilation, prosperity, longevity, nobility, harmony, reunion, success, loyalty, bravery, prosperity, romance, sexiness, enthusiasm, richness, euphemism; It has rich cultural connotation and lofty spiritual realm. People have devoted infinite love to it throughout the ages, and it is also favored by countries all over the world. With the continuous advancement of technology, Chinese red is gradually applied to daily life utensils, so that red porcelain, which can only be enjoyed by the royal family in ancient times, gradually enters our modern life. [0003] The reason why red porcelain is precious is not only its excellent luster and color, but also b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/86
Inventor 蔡金元
Owner CHAOZHOU QINGFA CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com