Polycarbonate composite material and preparation method thereof

A polycarbonate and composite material technology, applied in the field of polymer materials, can solve the problems of acid resistance, high molecular chain rigidity, and poor solvent resistance, and achieve good market application value, simple preparation method, and good hydrolysis resistance.

Inactive Publication Date: 2012-06-13
深圳市欧力隆科技有限公司
View PDF1 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has stable mechanical properties, dimensional stability, electrical properties and flame retardancy in a wide temperature range, and can be used for a long time at -60-120°C; has no obvious melting point, and is in a molten state at 220-230°C; molecular chain High rigidity, high viscosity of resin melt; small water absorption, small shrinkage, high dimensional accuracy, good dimensional stability, low air permeability of the film; self-extinguishing mater

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0029] Example 1

[0030] Weigh raw materials by weight percentage: PC resin 98.8%, dispersant 0.2%, hydrolysis-resistant agent AH210 0.1%, antioxidant 1076 0.3%, antioxidant 168 0.2%, lubricant EBS 0.4%.

[0031] Dry the PC resin in a blower dryer at a temperature of 110°C-130°C for 3-5 hours, add a dispersant and mix at high speed for 10 minutes, stop stirring, cool until the temperature drops to 30-35°C, and then add hydrolysis-resistant Agent, also mix at high speed for 10 minutes, then add antioxidant and processing aids and mix evenly at high speed. Through twin-screw extrusion and granulation, it can be cooled and granulated.

[0032] The granulator is a 35# twin-screw extruder, and the process parameters are: the temperature of the first zone is 130°C, the temperature of the second zone is 230°C, the temperature of the third zone is 235°C, the temperature of the fourth zone is 240°C, the temperature of the fifth zone is 240°C, and the temperature of the sixth zone is ...

Example Embodiment

[0033] Example 2

[0034] Weigh raw materials by weight percentage: PC resin 99.15%, dispersant 0.1%, hydrolysis resistance agent AH210 0.05%, antioxidant 1076 0.1%, antioxidant 168 0.1%, lubricant EBS 0.5%.

[0035] Dry the PC resin in a blower dryer at a temperature of 110°C-130°C for 3-5 hours, add a dispersant and mix at high speed for 10 minutes, stop stirring, cool until the temperature drops to 30-35°C, and then add hydrolysis-resistant Agent, also mix at high speed for 10 minutes, then add antioxidant and processing aids and mix evenly at high speed. Through twin-screw extrusion and granulation, it can be cooled and granulated.

[0036] The granulator is a 35# twin-screw extruder, and the process parameters are: the temperature of the first zone is 110°C, the temperature of the second zone is 225°C, the temperature of the third zone is 230°C, the temperature of the fourth zone is 235°C, the temperature of the fifth zone is 235°C, and the temperature of the sixth zone ...

Example Embodiment

[0037] Example 3

[0038] Weigh raw materials by weight percentage: PC resin 99.22%, dispersant 0.1%, hydrolysis-resistant agent AH210 0.08%, antioxidant 1076 0.2%, antioxidant 168 0.2%, lubricant EBS 0.2%.

[0039] Dry the PC resin in a blower dryer at a temperature of 110°C-130°C for 3-5 hours, add a dispersant and mix at high speed for 10 minutes, stop stirring, cool until the temperature drops to 30-35°C, and then add hydrolysis-resistant Agent, also mix at high speed for 10 minutes, then add antioxidant and processing aids and mix evenly at high speed. Through twin-screw extrusion and granulation, it can be cooled and granulated.

[0040] The granulator is a 35# twin-screw extruder, and the process parameters are: the temperature of the first zone is 120°C, the temperature of the second zone is 220°C, the temperature of the third zone is 230°C, the temperature of the fourth zone is 240°C, the temperature of the fifth zone is 230°C, and the temperature of the sixth zone i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polycarbonate composite material and a preparation method thereof. The polycarbonate composite material comprises, by weight, 98.7 to 99.3% of PC resin, 0.1 to 0.2% of a dispersing agent, 0.05 to 0.1% of a hydrolysis resistant agent, 0.2 to 0.5% of an anti-oxidant and 0.2 to 0.5% of a processing auxiliary agent. The polycarbonate composite material provided in the invention has high transparency and good hydrolysis resistance and is applicable in high-temperature high-humidity environments. The preparation method in the invention is simple, has an obvious improving effect, costs litter and has a good market application value.

Description

[technical field] [0001] The invention relates to the field of polymer materials, in particular to a polycarbonate composite material and a preparation method thereof. [Background technique] [0002] Bisphenol A aromatic polycarbonate (PC) is a colorless and transparent amorphous thermoplastic material. Chemical name: 2,2'-bis(4-hydroxyphenyl)propane polycarbonate. It has stable mechanical properties, dimensional stability, electrical properties and flame retardancy in a wide temperature range, and can be used for a long time at -60-120°C; has no obvious melting point, and is in a molten state at 220-230°C; molecular chain High rigidity, high viscosity of resin melt; small water absorption, small shrinkage, high dimensional accuracy, good dimensional stability, low air permeability of the film; self-extinguishing material; stable to light, but not resistant to ultraviolet light, good weather resistance ;Oil resistant, not resistant to acid, not resistant to strong alkali, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08L63/00C08K5/01C08K5/20B29C47/92B29B9/06B29C48/92
Inventor 徐东徐永付天英
Owner 深圳市欧力隆科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap