Plasties moulding compositions, mouldings and production processes
A technology of plastic mold and composition, applied in coating and other directions, can solve problems such as small gate, and achieve the effect of high surface quality, high transparency and excellent optical performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0112] Comparative Example 1 was essentially repeated, except that Inventive Example 1 used a plastics molding composition prepared as follows: about 33% by weight of PMMA molding composition A) having a melt flow rate of about 21 ml / 10 minutes (may Product name POQ62 from Evonik GmbH) and approximately 67% by weight of an impact modifier that imparts high die swell to the plastic molding composition (available under the trade name zk50 from Evonik GmbH commercially) compounding (mixing in the melt).
[0113] The properties of the plastics moulding compositions were investigated using the methods described above, and the haze was also evaluated here for mouldings having a thickness of 1 mm. The data obtained are shown in Table 1.
Embodiment 2
[0123] Comparative Example 1 was essentially repeated, except that Inventive Example 2 used a plastics molding composition prepared as follows: about 50% by weight of PMMA molding composition A)( Can trade name POQ62 from Evonik GmbH) and approximately 50% by weight of an impact modifier that imparts high die swell to the plastic molding composition (available under the trade name zk50 from Evonik GmbH commercially) compounding (mixing in the melt).
[0124] The properties of the plastics moulding compositions were investigated using the methods described above, and the haze was also evaluated here for mouldings having a thickness of 1 mm. The data obtained are shown in Table 1.
[0125] Table 1
[0126]
[0127] Table 1 (continued)
[0128]
[0129] The data presented above clearly reveal that a haze of less than 1% can be obtained in samples with a thickness of 1 mm only when the composition according to the invention is used. These data can be achieved inde...
PUM
Property | Measurement | Unit |
---|---|---|
glass transition temperature | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap