Especially iron bases for steam irons

A technology for irons and substrates, applied in hand irons, applications, household appliances, etc., can solve the problems that the coloring pattern cannot be adhered to sufficiently for a long time, and no aluminum substrate is found, so as to save manufacturing costs and costs, and reduce the contact surface , the effect of improving the distribution

Inactive Publication Date: 2015-09-16
BSH BOSCH & SIEMENS HAUSGERAETE GMBH
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] As soon as an attempt was also made to print coloring patterns on anodized aluminum substrates, it quickly became apparent that due to multiple operations of the iron, the coloring patterns did not adhere permanently enough, so that in practice no printed coloring patterns were found due to quality defects anodized aluminum base

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Especially iron bases for steam irons
  • Especially iron bases for steam irons

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] figure 1 The surface 11 of the iron base 10 of the steam iron 1 is schematically shown, which is opened by openings 13 for the passage of steam.

[0029] The surface 11 of the substrate 10, which is at least designed to come into contact with the item to be ironed, is made, for example, of rolled aluminium, which is then electrolytically oxidized. In this case, a thin native oxide layer forms already after a short time in air due to the high affinity of aluminum for oxygen. The process ends after a few months and forms an oxide layer so thick that oxygen diffusion is no longer possible. The layer then reaches a thickness of about 0.05 μm and does not expand any further. However, smaller layer thicknesses do not provide sufficient protection. Therefore, the aluminum is protected on the surface 11 with a thick aluminum oxide layer, which is called ELOXAL (electrolytic aluminum oxide) in German, by anodizing in the electrolyte. The method is technically known specifica...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The present invention relates to an iron soleplate (10) and to a method for the production thereof, in particular for a steam iron (1), the surface (11) of which provided for placement on objects to be iron consists of anodized aluminum and / or is coated with an anodized aluminum layer. In order to improve the ironing and gliding properties, a raised enamel graphics element (20) is applied to the anodized aluminum surface (11), which element can preferably contain color pigments of a silicate dye, in which in particular the silicon components were replaced with aluminum. The present invention surprisingly improves the prior art of iron soleplates (10), wherein at least the surface (11) consists of anodized aluminum.

Description

technical field [0001] The invention relates to an iron base, in particular for a steam iron, and a method for producing the same, the surface of which is intended to be applied to an object to be ironed made of anodized aluminum formed and / or covered with an anodized aluminum layer. Background technique [0002] It is known to have iron bases made of metal, the surface of which is provided for application to an object to be ironed is polished. Because it proceeds from this: the best method for obtaining high ironing quality consists in using a substrate whose surface roughness is as small as possible in order to obtain a good heat transfer between the substrate and the object to be ironed and at the same time reduce Small coefficient of friction, which improves the "slide" of the iron on the object. [0003] However such polished substrates are prone to scratching or spotting, especially when the substrate is made of aluminum or covered with an aluminum layer. [0004] T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D06F75/38C25D11/18
CPCC25D11/04C25D11/18B41M1/28D06F75/38
Inventor C.阿尔万多斯鲁伊斯德奥森达
Owner BSH BOSCH & SIEMENS HAUSGERAETE GMBH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap