Protecting-treating technology for metal surface

A treatment process and metal surface technology, applied in the direction of metal material coating process, etc., can solve the problems of weak adhesion, easy detachment, pollution of the environment, etc., to achieve good metal surface pretreatment, low polarization current density, and enhanced adhesion. Effect

Inactive Publication Date: 2015-03-04
蚌埠市钰诚五金工贸有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] There are many coating protection methods for metal surfaces, such as coating organic coatings or coatings on metal surfaces, passivation, phosphating treatment, metal surface protective agents produced by traditional processes, film layers and metal bodies formed during use. The adhesion is weak, easy to detach, the film layer structure is not dense enough, the protection efficiency of the metal is greatly reduced, and some will produce waste water during production and use, polluting the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Protecting-treating technology for metal surface

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] A metal surface protection treatment process, specifically comprising the following steps:

[0034] 1), first degrease the surface of the metal workpiece;

[0035] 2) Wash the metal workpiece twice with water after degreasing;

[0036] 3) The washed metal workpiece is polished with metallographic sandpaper;

[0037] 4) The polished metal workpiece is degreased again, and then washed for the third time;

[0038] 5) Apply silane solution to the workpiece washed three times;

[0039] 6) The workpiece coated with silane solution is blown dry with compressed air, and then cured at room temperature.

[0040] Wherein, for the silane solution described in step 5), the components and weight per liter of the silane solution are:

[0041] Silane coupling agent KBM602 30g

[0042] Phytic acid 2g

[0043] Triethanolamine 6g

[0044] Ammonium molybdate 0.15g

[0045] Sodium metasilicate 6g

[0046] Ethanol 100g

[0047] The balance is water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a protecting-treating technology for a metal surface. The protecting technology comprises the following steps: firstly, performing conventional degreasing on a metal piece for one time; performing water washing for two times; performing sanding; performing degreasing and water washing again; coating silane solution; and coating after curing, thereby finishing the protecting technology. After the metal piece is treated according to the protecting technology, a poly-acid film layer is formed on the surface of the metal piece; the film layer is compact and uniform, is strong in adhesive force with metal body and is difficult to drop; the protecting efficiency on metal is increased; and meanwhile, the operating process is environment-friendly and pollution-free.

Description

technical field [0001] The invention relates to the field of metal surface treatment, in particular to a metal surface protection treatment process. Background technique [0002] With the wide application of metal products in industry and life, the corresponding metal corrosion is also becoming more and more serious. Therefore, various anti-corrosion technologies are also widely used in metal processing, among which metal surface coating protection technology is the most widely used and most effective. [0003] There are many coating protection methods for metal surfaces, such as coating organic coatings or coatings on metal surfaces, passivation, phosphating treatment, metal surface protective agents produced by traditional processes, film layers and metal bodies formed during use. The adhesion is weak, it is easy to detach, the film structure is not dense enough, the protection efficiency of the metal is greatly reduced, and some will produce waste water during product...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C22/73C23C22/68C23C22/40
Inventor 陈云帮丁宁庞志成丁旬刘传让徐大力朱泽光
Owner 蚌埠市钰诚五金工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products