Capsaicin antifouling paint for preventing marine organisms from growing in intertidal region and construction process thereof

A technology of capsaicin and antifouling paint, which is applied in the field of anti-sea organisms and anti-corrosion construction engineering, to achieve the effect of solving heavy pollution and improving safety

Active Publication Date: 2012-09-19
JIANGSU LONGYUAN OFFSHORE WIND POWER GENERATION
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no precedent for the use of capsaicin antifouling paint in this area in China. In order to prevent the growth of mar...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Embodiment one: capsaicin antifouling paint is that paint is mixed with high-purity capsaicin solution and stirred to form, and the weight percent content of high-purity capsaicin solution in capsaicin antifouling paint is 0.6%, the weight of high-purity capsaicin in high-purity capsaicin solution The percentage content is 80%, and the weight percentage content of the capsaicin in the high-purity capsaicin is more than 98%.

[0012] A construction process using the above-mentioned capsaicin antifouling paint for preventing the growth of marine organisms in the intertidal zone, in which the capsaicin antifouling paint is coated on the outer surface of the fan foundation in the anti-corrosion construction project of marine organisms in the offshore wind power industry to form anti-corrosion Coating, the thickness of anti-corrosion coating is 800μm.

[0013] Test: The capsaicin antifouling paint of Example 1 was coated on the outer surface of the test foundation similar to...

Embodiment 2

[0014] Embodiment two: capsaicin antifouling paint is that paint mixes high-purity capsaicin solution and stirs to form, and the weight percent content of high-purity capsaicin solution in capsaicin antifouling paint is 0.7%, and the weight of high-purity capsaicin solution in high-purity capsaicin solution The percentage content is 85%, and the weight percentage content of the capsaicin in the high-purity capsaicin is more than 98%.

[0015] A construction process using the above-mentioned capsaicin antifouling paint for preventing the growth of marine organisms in the intertidal zone, in which the capsaicin antifouling paint is coated on the outer surface of the fan foundation in the anti-corrosion construction project of marine organisms in the offshore wind power industry to form anti-corrosion Coating, the thickness of anti-corrosion coating is 900μm.

[0016] Test: The capsaicin antifouling paint of Example 1 was coated on the outer surface of the test foundation similar...

Embodiment 3

[0017] Embodiment three: capsaicin antifouling paint is that the paint is mixed with high-purity capsaicin solution and stirred to form, and the weight percentage content of high-purity capsaicin solution in the capsaicin antifouling paint is 0.8%, the weight of high-purity capsaicin in the high-purity capsaicin solution The percentage content is 90%, and the weight percentage content of the capsaicin in the high-purity capsaicin is more than 98%.

[0018] A construction process using the above-mentioned capsaicin antifouling paint for preventing the growth of marine organisms in the intertidal zone, in which the capsaicin antifouling paint is coated on the outer surface of the fan foundation in the anti-corrosion construction project of marine organisms in the offshore wind power industry to form anti-corrosion Coating, the thickness of anti-corrosion coating is 1000μm.

[0019] Test: The capsaicin antifouling paint of Example 1 was coated on the outer surface of the test fou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a capsaicin antifouling paint for preventing marine organisms from growing in an intertidal region. The capsaicin antifouling paint is used for forming a corrosion-resistant costing on the outer surface of a fan foundation in anti-marine organism corrosion prevention construction engineering in the offshore wind power industry; the capsaicin antifouling paint is formed by doping an oil paint with a high-purity capsaicin solution and stirring; the weight percentage content of the high-purity capsaicin solution in the capsaicin antifouling paint is 0.6-0.8 percent; the weight percentage content of high-purity capsaicin in the high-purity capsaicin solution is 80-90 percent; and the weight percentage content of capsaicin in the high-purity capsaicin is over 98 percent. In a construction process for constructing by adopting the capsaicin antifouling paint for preventing marine organisms from growing in an intertidal region, the capsaicin antifouling paint is coated onto the outer surface of a fan foundation in anti-marine organism corrosion prevention construction engineering in the offshore wind power industry to form a corrosion-resistant coating. Due to the adoption of the capsaicin antifouling paint, the safety of an offshore fan foundation is enhanced greatly.

Description

technical field [0001] The invention relates to the technical field of anti-sea organisms and anti-corrosion construction engineering in the offshore wind power industry, in particular to a capsaicin antifouling paint for preventing the growth of sea organisms in an intertidal zone and a construction process thereof. Background technique [0002] Due to the ebb and flow of tides and the alternation of dry and wet conditions in the intertidal zone, sea organisms grow seriously in the tidal zone, which has a negative impact on the appearance of the fan foundation, anti-corrosion coating and foundation load. At present, there is no domestic precedent of using capsaicin antifouling paint in this area. In order to prevent the growth of marine organisms in this area, a capsaicin antifouling paint and its construction technology suitable for this area have been specially developed. Utility model content [0003] The technical problem to be solved by the present invention is to ov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/16C09D5/08C09D7/12C09D175/04C09D127/24C09D123/28
Inventor 张钢高宏飙陈强刘碧燕季晓强
Owner JIANGSU LONGYUAN OFFSHORE WIND POWER GENERATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap