A kind of piezoelectric material and preparation method thereof

A piezoelectric material and pressure technology, applied in piezoelectric/electrostrictive/magnetostrictive devices, circuits, electrical components, etc., can solve problems such as high resonance impedance coupling coefficient, low mechanical Q value, high sensitivity, etc., to achieve Effects of improving piezoelectric performance, reducing Qm value, and increasing piezoelectric coefficient

Active Publication Date: 2014-10-08
WUXI ZHONGKE ULTRASONIC TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The ceramic material has extremely low mechanical Q value, high sensitivity, high resonance impedance and suitable coupling coefficient, dielectric constant, and low cost, but the ceramic material does not involve the aspect of piezoelectric coefficient d33

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of piezoelectric material and preparation method thereof
  • A kind of piezoelectric material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] (1) Select compounds containing the required elements (PbO, BaO, MgO, NiO, TiO 2 , ZrO 2 , Nb 2 o 5 ), batching according to the chemical composition of the compound to be prepared, pre-pressing after ball milling, pre-calcining, rolling ball milling again, to obtain substance a;

[0051] (2) Adding a binder to substance a to granulate, forming and discharging plastic, and then sintering to obtain substance b;

[0052] (3) Substance b is subjected to polarization treatment to obtain a piezoelectric material with the following chemical composition: Pb 0.98 Ba 0.01 Mg 0.01 [(Ni 1 / 3 Nb 2 / 3 ) 0.1 · Zr 0.6 · Ti 0.3 ]O 3 .

[0053] The mass of the compound containing the desired elements can be calculated from the chemical composition of the final piezoelectric material.

Embodiment 2

[0055] (1) Select compounds containing the required elements (lead carbonate, strontium carbonate, magnesium carbonate, NiO, Nb 2 o 5 , zirconium carbonate, titanium nitride), according to the chemical composition of the compound to be prepared, the ingredients are pre-pressed after ball milling, pre-calcined, and ball milled again to obtain substance a;

[0056] (2) Adding a binder to substance a to granulate, forming and discharging plastic, and then sintering to obtain substance b;

[0057] (3) Substance b is subjected to polarization treatment to obtain a piezoelectric material with the following chemical composition: Pb 0.9 Sr 0.05 Mg 0.05 [(Ni 1 / 3 Nb 2 / 3 ) 0.7 · Zr 0.2 · Ti 0.1 ]O 3 .

[0058] The mass of the compound containing the desired elements can be calculated from the chemical composition of the final piezoelectric material.

Embodiment 3

[0060] (1) Select compounds containing the required elements (lead carbonate, lanthanum carbonate, barium carbonate, NiO, Nb 2 o 5 , titanium nitrate, zirconium nitrate), ingredients according to the chemical composition of the compound to be prepared, pre-pressed after ball milling, pre-calcined, rolling ball milling again, to obtain substance a;

[0061] (2) Adding a binder to substance a to granulate, forming and discharging plastic, and then sintering to obtain substance b;

[0062] (3) Substance b is subjected to polarization treatment to obtain a piezoelectric material with the following chemical composition: Pb 0.95 La 0.02 Ba 0.03 [(Ni 1 / 3 Nb 2 / 3 ) 0.2 · Zr 0.1 · Ti 0.7 ]O 3 .

[0063] The mass of the compound containing the desired elements can be calculated from the chemical composition of the final piezoelectric material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
dielectric lossaaaaaaaaaa
electromechanical coupling coefficientaaaaaaaaaa
Login to View More

Abstract

The invention relates to a piezoelectric material and a preparation method thereof. The chemical composition of the piezoelectric material is as follows: Pb1-x-yMe1xMe2y[(Ni1 / 3Nb2 / 3)a·Zrb·Tic]O3, wherein Me1 and Me2 is independently selected from one or a combination of at least two of Ba, Ca, Sr, Mg, La; x+y=0.02~0.1; a is 0.1~0.7; b is 0.1~0.6; c is 0.1~0.8 , and a+b+c=1. The piezoelectric material of the present invention has the advantages of high voltage coefficient and low mechanical quality factor, and has other excellent properties, and can be widely used in high-sensitivity flow meter sensors, piezoelectric speakers, brakes, micro-positioning systems, Hydroacoustic engineering, passive sonar and other fields.

Description

technical field [0001] The invention relates to a piezoelectric material, in particular to a piezoelectric material with a high piezoelectric coefficient d33 and a low mechanical quality factor Qm and a preparation method thereof. Background technique [0002] Materials can be divided into two categories: structural materials and functional materials in terms of performance. Among them, structural materials are based on their mechanical properties such as strength, toughness, hardness, and elasticity. Functional materials are based on their electrical, magnetic, optical, sound, thermal, etc. Based on physical properties, it is used to make devices with special functions. Piezoelectric materials are functional materials that convert mechanical energy to electrical energy. They are electronic materials that are sensitive to mechanics, electricity, sound, light, and heat. They are widely used in industrial sectors and high-tech fields. [0003] Piezoelectric materials are divi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/491C04B35/472C04B35/499C04B35/622C04B35/634H01L41/187H10N30/853