Formula of jewelry cleanser and preparation method

A cleaning agent and jewelry technology, applied in the formulation of cleaning agents and its preparation field, can solve the problems of shortening the life of the jewelry, difficult to clean, easy to damage the surface of the jewelry, etc., and achieves improved decontamination, strong decontamination effect and stability. strong effect

Active Publication Date: 2013-06-05
GUANGDONG CHJ IND
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If it is cleaned with ordinary detergent, it is not only difficult to clean, but also easily damages the surface of the jewelry and shortens the life of the jewelry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of jewelry cleaning agent containing nano colloidal silicon, its preparation method comprises the following steps:

[0021] (1) Add 100g of propylene glycol and 100g of hydroxymethyl cellulose to 1600g of deionized water while stirring to make them evenly dispersed, and heat to 50-60°C;

[0022] (2) Add 100g of sodium dodecylbenzenesulfonate and 150g of triethanolamine stearate quaternary ammonium salt, stir to make it fully dissolve and then cool down to 25°C;

[0023] (3) Then slowly add 50 g of nano-colloidal silicon dispersant with a diameter of 7 nm and a solid content of 30 wt % while stirring to make it evenly dispersed, and pack it for use.

[0024] It can be used with water when in use, or it can be sprayed directly on a cloth to wipe the jewelry.

Embodiment 2

[0026] A kind of jewelry cleaning agent containing nano colloidal silicon, its preparation method comprises the following steps:

[0027] (1) Weigh the following substances by weight: 4-6 nano colloidal silicon dispersants with a solid content of 30wt%, 8-15, 8-15 propylene glycol, 8-15 hydroxymethylcellulose, triethanolamine stearate Quaternary ammonium salt 10-20, deionized water 140-180. 1-10 nano colloidal silicon dispersants with a solid content of 30wt%, 1-20 propylene glycol, 1-20 alkylbenzene sulfonates, 1-20 hydroxymethyl cellulose, 5-30 triethanolamine stearate quaternary ammonium salts , Deionized water 100-200.

[0028] (1) Add 10-80g propylene glycol and 10-80g hydroxymethyl cellulose to 1000-1400g deionized water while stirring to make them evenly dispersed, and heat to 50-60°C;

[0029] (2) Add 50-80g of sodium dodecylbenzenesulfonate and 50-100g of triethanolamine stearate quaternary ammonium salt, stir to make it fully dissolve and then cool down to 25°C;

...

Embodiment 3

[0033] (1) Weigh the following substances by weight: 4-6 nano colloidal silicon dispersants with a solid content of 30wt%, 8-15, 8-15 propylene glycol, 8-15 hydroxymethylcellulose, triethanolamine stearate Quaternary ammonium salt 10-20, deionized water 140-180. 1-10 nano colloidal silicon dispersants with a solid content of 30wt%, 1-20 propylene glycol, 1-20 alkylbenzene sulfonates, 1-20 hydroxymethyl cellulose, 5-30 triethanolamine stearate quaternary ammonium salts , Deionized water 100-200.

[0034] (1) Add 150-200g of propylene glycol and 150-200g of hydroxymethyl cellulose to 1800-2000g of deionized water while stirring to make them evenly dispersed, and heat to 50-60°C;

[0035] (2) Add 150-200g of sodium dodecylbenzenesulfonate and 200-300g of triethanolamine stearate quaternary ammonium salt, stir to make it fully dissolve and then cool down to 25°C;

[0036] (3), then slowly add 60-100g of nano-colloidal silicon dispersant with a diameter of 7nm and a solid content...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a formula of a jewelry cleanser. The formula comprises the following components in parts by weight: 1-10 parts of nanometer colloidal silica dispersant with solid content of 30 percent by weight, 1-20 parts of propylene glycol, 1-20 parts of alkylbenzene sulfonate, 1-20 parts of hydroxymethyl cellulose, 5-30 parts of stearic acid triethanolamine ester quaternary ammonium salt and 100-200 parts of de-ionized water. The invention also discloses a method of preparing the jewelry cleanser. The method comprises the following steps of: (1) adding the propylene glycol and thehydroxymethyl cellulose into the de-ionized water with stirring in sequence and uniformly dispersing the propylene glycol and the hydroxymethyl cellulose, and heating to 50-60 DEG C; (2) adding the alkylbenzene sulfonate and the stearic acid triethanolamine ester quaternary ammonium salt, stirring to fully dissolve the alkylbenzene sulfonate and the stearic acid triethanolamine ester quaternary ammonium salt and cooling to 25 DEG C; and (3) slowly adding the nanometer colloidal silica dispersant with stirring and uniformly dispersing the nanometer colloidal silica dispersant. The various components of the jewelry cleanser are environment-friendly; and the jewelry cleanser has the advantages of extremely high antifouling effect, high stability and capability of polishing the metal. The jewelry cleanser has a good effect of cleaning the surfaces of precious metals and various jewelries.

Description

technical field [0001] The invention relates to a cleaning agent, in particular to a formula for cleaning various jewelry and a preparation method thereof. Background technique [0002] Under the long-term action of oxygen, moisture, etc., the surface of jewelry will become black and dark, promoting luster. If it is cleaned with ordinary detergent, it is not only difficult to clean, but also easily damages the surface of the jewelry and shortens the life of the jewelry. Contents of the invention [0003] In view of the problems raised above, the object of the present invention is to provide a formula and a preparation method of a jewelry cleaning agent that has a strong decontamination effect, strong stability, and can make metal bright. [0004] The present invention is achieved through the following technical measures, a jewelry cleaning agent, comprising the following components by weight: 1-10 nano colloidal silicon dispersants with a solid content of 30wt%, 1-20 prop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C11D1/65C11D1/86C11D3/20C11D3/22C11D3/60
Inventor 廖创宾
Owner GUANGDONG CHJ IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap