Lead-carbon battery anode lead paste for hybrid vehicle, and its preparation method

A technology for hybrid electric vehicles and lead-carbon batteries, which is applied to battery electrodes, circuits, electrical components, etc. It can solve the problems of softening of the active material of the positive plate and the end of battery life, and achieve the effect of strong charge acceptance and excellent cycle life

Inactive Publication Date: 2012-10-17
TIANNENG GRP JIANGSU TECH
View PDF6 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with the prolongation of the cycle life of the negative plate, the active material of the positive plate of the battery will soften, which will eventually lead to the end of the battery life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lead-carbon battery anode lead paste for hybrid vehicle, and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Take lead powder by weight: 100 parts, sulfuric acid: 10 parts, fumed silica: 1 part, cerium oxide: 0.5 parts, yttrium oxide: 0.25 parts, red lead: 4 parts, red powder: 4 parts, spherical graphite: 0.5 parts, glass fiber: 0.5 parts, water: 12 parts.

[0025] Prepare the positive lead paste as follows:

[0026] (1) Accurately weigh lead powder, fumed silica, rare earth oxide, red lead, red powder, spherical graphite, and glass fiber into a custom-made container, and stir for 5-10 minutes to fully mix the components.

[0027] (2) Quickly add water into the container containing step (1) mixing, and stir for 5-10 minutes during the process.

[0028] (3) Slowly add sulfuric acid into the container of step (2) for 8-15 minutes, stir during the process, and control the temperature below 70°C; after the sulfuric acid is completely added, stir for 5-10 minutes.

[0029] (4) Add the prepared organic binder into the container in step (3), stir for 5-10 minutes, and control the a...

Embodiment 2

[0039] Take lead powder by weight: 100 parts, sulfuric acid: 4 parts, fumed silica: 3 parts, cerium oxide: 0.5 part, red lead: 0.1 part, red powder: 0.1 part, heterogeneous graphite: 0.1 part, glass fiber: 0.1 parts, water: 15 parts.

[0040] All the other implementations are as in Example 1.

Embodiment 3

[0042] Take lead powder by weight: 100 parts, sulfuric acid: 7 parts, fumed silica: 0.1 part, cerium oxide, yttrium oxide, europium oxide mixed in 1:1:1: 2 parts, red lead: 2 parts, red powder: 2 parts, spherical graphite, nano-graphite (mixed at 1:1): 2 parts, glass fiber: 1 part, water: 18 parts.

[0043] All the other implementations are as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a lead-carbon battery anode lead paste for a hybrid vehicle. The lead paste is obtained through mixing the following raw materials, by weight, 100 parts of lead powder, 4-15 parts of sulfuric acid, 0.05-5 parts of fumed silica, 0.05-3 parts of a rare earth oxide, 0.1-10 parts of red lead, 0.1-10 parts of Hydrargyri Oxydum Rubrum, 0.1-4 parts of graphite, 0.1-2 parts of a short fiber, and 10-20 parts of water. According to the invention, the fumed silica and the rare earth oxide are added to the lead paste, and other anode additives are also added to prepare the novel lead paste, a pole plate can be coated under a routine lead-acid battery production coating facility condition, the anode is obtained after curing, and there is very good adhesion between an active substances and a plate grid, and one active substance and another active substance, so the electrical properties of the battery are excellent.

Description

Technical field [0001] The invention involves the field of battery production and specially involves a mixed -power car charcoal battery cream and its preparation method. Background technique [0002] Because the hybrid vehicle battery is in some load -long state, shallow charge, high charging and discharge frequency, and large current, it is easy to cause negative vulcanosulfate, which will fail the battery.Patent CN101969149A proposes that adhesives and carbon materials are added to the conventional battery formula's negative lead cream formula, which will significantly delay the negative electrode sulfate.Studies have found that after the above materials are added to the negative lead paste, the negative vulcanosulfate is suppressed, the battery's large current charging discharge performance is improved, and the cycle life of the hybrid vehicle operation mode is significantly prolonged.However, with the extension of the loop life of the negative plate, the battery will soften ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/62H01M4/56
CPCY02E60/12Y02E60/10
Inventor 陈飞杨惠强方明学梁佳翔宫江平赵冬冬
Owner TIANNENG GRP JIANGSU TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com