Boron-containing micro-alloy weather resisting steel and manufacturing method thereof

A technology of atmospheric corrosion-resistant steel and a manufacturing method, applied in the field of continuous casting technology, can solve the problems of poor formability, uneven structure and high yield ratio
CN102787279AActive Publication Date: 2012-11-21BAOSHAN IRON & STEEL CO LTD
28 Cites 22 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
BAOSHAN IRON & STEEL CO LTD
Publication Date
2012-11-21

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention relates to boron-containing micro-alloy weather resisting steel and a manufacturing method thereof. The boron-containing weather resisting steel is continuously cast by a twin-roll thin strip, a cast strip is uniformly reinforced and cooled by spraying dry ice after exiting a crystallization roll, the cast strip is rapidly cooled to the temperature lower than 1280 DEG C at the speed of 200-300 DEG C / s, precipitation of thick BN can be promoted in the cooling mode, B2O3 with a low melting point and precipitation of thin AlN are prevented, accordingly, austenite crystal grains are homogenized, and the yield ratio is reduced. Online austenite recrystallization rolling and anti-oxidation rapid cooling at the speed of 80-200 DEG C / s are performed, and the coiling temperature is 500-600 DEG C. The steel with the low yield ratio can be obtained, and the ubiquitous problem that steel continuously cast by a thin strip is inhomogeneous in structure, high in yield ratio, difficult in forming and incapable of meeting the requirement of cold rolling of materials is solved.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a continuous casting process, in particular to a boron-containing micro-alloy steel resistant to atmospheric corrosion and a manufacturing method thereof. Background technique

[0002] Traditional thin strips are mostly produced by multi-pass continuous rolling of cast slabs with a thickness of 70-200mm, while cast strips produced by twin-roll thin strip continuous casting process are rolled into hot strips in one or two passes. The rolled strip can be put into the market. Compared with the traditional strip production process, the former has a shorter production line and requires less energy. It is a low-carbon and environmentally friendly hot-rolled thin strip production process.

[0003] The typical technological process of twin-roll thin strip continuous casting is: molten steel in the ladle is poured directly into a crystallization roller and side sealing device that rotates relatively and can be cooled rapidly through th...