Method for manufacturing free-cutting stainless steel wire for ball-point pen head

A technology of stainless steel wire and manufacturing method, which is applied in the field of manufacturing easy-to-cut stainless steel wire for ballpoint pen heads, and can solve the problems of poor corrosion resistance and wear resistance

Active Publication Date: 2012-12-19
NINGBO BEIFA GRP CO LTD
View PDF5 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The ballpoint pen head material was first made of lead brass, but its corrosion resistance and wear resistance were poor, and it was gradually replaced by nickel-nickel copper, but the...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] Below in conjunction with embodiment the present invention is described in further detail.

[0015] A method for manufacturing a free-cutting stainless steel wire for a ballpoint pen head, comprising the following steps:

[0016] 1) Film treatment: The surface of Ф5.5mm stainless steel wire is treated with film in the film tank equipped with film agent, wherein the Ф5.50mm stainless steel wire is mainly composed of alloy elements in the following weight percentages: C0.016%, Si0.33%, Mn1.02%, P0.005%, S0.32%, Cr20.57%, Mo1.71%, Pb0.22%, Te0.04%, Al0.002, Nb0.01, Ti0. 01, the balance is Fe and unavoidable impurities, the temperature of the coating agent is 90°C, and the coating treatment time is 30 minutes;

[0017] 2) Drying: Dry the stainless steel wire after film treatment at 150°C for 40 minutes;

[0018] 3) The first drawing and the first online bright annealing: the first drawing is carried out on the stainless steel wire after film treatment and drying, and then...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for manufacturing the free-cutting stainless steel wire for a ball-point pen head, comprising the following steps: (1) treating the skin film; (2) drying; (3) drawing for the first time and carrying out bright annealing on line for the first time, wherein the area-reduction rate during drawing for the first time is 40-60%, the temperature of carrying out bright annealing on line for the first time is 700-900 DEG C, and the annealing speed is 3-9m/min; (4) drawing for the second time and carrying out bright annealing on line for the second time, wherein the area-reduction rate during drawing for the second time is 40-60%, the temperature of carrying out bright annealing on line for the second time is 700-900 DEG C, and the annealing speed is 5-12m/min; and (5) drawing for the third time, wherein the area-reduction rate during drawing for the third time is 25-45%. The free-cutting stainless steel wire manufactured by the method has a bright surface, is free from the defects of black and yellow lines, drawing stamps, cracks, folding lines, peeling and the like and has the following mechanical properties: the yield strength of 500-800N/mm<2>, the tensile strength of 700N/mm<2> or higher, the elongation of 3-6% and the hardness value (HV) of 240-280.

Description

technical field [0001] The invention relates to a manufacturing method of stainless steel wire, in particular to a manufacturing method of free-cutting stainless steel wire for a ball point pen head. Background technique [0002] According to the performance of the ink used, ballpoint pens are divided into five types: oily, water-based, pressure, ball-ball and erasable. A ballpoint pen is generally composed of a pen stem, a refill, and oil (water) ink. The refill is composed of five parts: a ball, a ball seat, an oil pipe, ink, and a floating plug. The functions of sliding, adhering and carrying oil (water) ink to the paper surface to complete the writing record. [0003] In the past, the balls were made of stainless steel, but now they are mostly made of hard alloy. The surface of the ball has high hardness, wear resistance and corrosion resistance, and the surface is densely covered with uniform micropores, which is easy to absorb ink and achieve uniform ink output and sm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/22C21D8/06
Inventor 蒋超贺丹红袁方明戴泽千谢大凯
Owner NINGBO BEIFA GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap