High-voltage insulation ceramic ash glaze formula

A high-pressure porcelain and formula technology, applied in the field of electric porcelain, can solve the problems of poor mechanical, electrical and thermal performance of electric porcelain, unsatisfactory chemical corrosion resistance and anti-fouling performance, and can not greatly improve the mechanical and electrical properties of porcelain. problem, to achieve the effect of fine and bright glaze color and improve appearance quality

Inactive Publication Date: 2012-12-26
CHONGQING PIGEON ELECTRIC PORCELAIN CO LTD
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the traditional gray glaze for electric porcelain, after glazing, is not effective in improving the mechanical, electrical and thermal properties of electric porcelain, especially it cannot greatly improve the mechanical and electrical properties of porcelain, and at the same time, the chemical corrosion resistance and antifouling performance are also poor. not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The components and parts by weight ratio included in the formula of this embodiment are:

[0019] Potassium feldspar 26

[0020] Quartz Powder 20

[0021] Kaolin 16

[0022] Xinhui kaolin 4

[0023] limestone 6

[0024] Forged talc 6

[0025] Zirconium silicate 2.5

[0026] Gray glaze color base 0.6

[0027] Barium Carbonate 1.5

[0028] Wherein, the Xinhui kaolin is the kaolin provided by Sibi Kejia Kiln Company, and the specific components are known components, which will not be repeated here.

[0029] After testing, the gray glaze made according to the components and weight ratio of this embodiment can increase the strength of electric porcelain by more than 20% after glazing, make the strength of ordinary porcelain reach 150MPa, and make the strength of high-strength porcelain reach 225MPa.

Embodiment 2

[0031] The components and parts by weight ratio included in the formula of this embodiment are:

[0032] Potassium feldspar 30

[0033] Quartz powder 24

[0034] Kaolin 20

[0035] Xinhui Kaolin 6

[0036] limestone 10

[0037] Forged talc 8

[0038] Zirconium silicate 4

[0039] Gray glaze color base 0.8

[0040] barium carbonate 4

[0041] Wherein, the Xinhui kaolin is the kaolin provided by Sibi Kejia Kiln Company, and the specific components are known components, which will not be repeated here.

[0042] After testing, the gray glaze made according to the components and weight ratio of this embodiment can increase the strength of electric porcelain by more than 20% after glazing, make the strength of ordinary porcelain reach 155MPa, and make the strength of high-strength porcelain reach 210MPa.

[0043] In summary, the electric porcelain gray glaze produced by the high-voltage porcelain insulating gray glaze formula of the present invention can greatly improve the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-voltage insulation ceramic ash glaze formula which comprises the following components in parts by weight: 26-30 parts of potash feldspar, 20-24 parts of quartz powder, 16-20 parts of kaolin, 4-6 parts of Xinhui kaolin, 6-10 parts of limestone, 6-8 parts of forged talcum, 2.5-4 parts of zirconium silicate, 0.6-0.8 part of ash glaze color base and 1.5-4 parts of barium carbonate. The electric ceramic ash glaze produced according to the formula disclosed by the invention is suitable to be applied on suspended, rod-like, sleeve and other types of ceramic insulators, can greatly enhance the mechanical, electrical and thermal properties of ceramic, and enhances the appearance quality of the high-voltage ceramic, so that the insulator has fine and bright glaze color.

Description

technical field [0001] The invention belongs to the technical field of electric porcelain, and in particular relates to a high-voltage porcelain insulating gray glaze formula. Background technique [0002] For the glazing of high-voltage porcelain insulators, the pursuit is to comprehensively improve the mechanical, electrical and thermal performance of porcelain insulators, improve the appearance quality of high-voltage porcelain insulators, and then improve the service life of porcelain insulators. However, the traditional gray glaze for electric porcelain, after glazing, is not effective in improving the mechanical, electrical and thermal properties of electric porcelain, especially it cannot greatly improve the mechanical and electrical properties of porcelain, and at the same time, the chemical corrosion resistance and antifouling performance are also poor. not ideal. Contents of the invention [0003] The technical problem to be solved by the present invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 姚绍明罗汉英
Owner CHONGQING PIGEON ELECTRIC PORCELAIN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com