Low-retraction silicane XLPE (Cross Linked Polyethylene) insulating material of 10 KV and below applicable to extrusion one-step method

An extruded and insulating material technology, which is applied in the direction of organic insulators, plastic/resin/wax insulators, etc., can solve the problems of wide range of additive types and dosages, little reference value, and no disclosure of specific grades of base resins, etc. , to achieve simple and effective control of insulation shrinkage test performance, good practicability and reference value, and small shrinkage

Active Publication Date: 2014-07-16
FAR EAST CABLE +2
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] Chinese invention application 200510026418.0 discloses a "silane cross-linked low-shrinkage polyethylene plastic and its preparation method and application", which discloses two-step silane cross-linked polyethylene, not one-step silane cross-linked polyethylene; it discloses The process is suitable for production by extrusion dies, but not by extrusion dies; the base material it discloses is a combination of several resins, not a single resin; it does not disclose the specific grades of base resins, types of additives and The indicated range of dosage is too wide, and the actual reference value is not great
[0017] Chinese invention application 201010160172 discloses a "one-step silane cross-linked polyethylene cable material", which is not a low-retraction type silane cross-linked polyethylene cable material with an insulation shrinkage rate below 4%; the base material it discloses is The two resins are used together, not a single resin; it does not disclose the specific grade of the base resin, and the reference value is not great

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-retraction silicane XLPE (Cross Linked Polyethylene) insulating material of 10 KV and below applicable to extrusion one-step method
  • Low-retraction silicane XLPE (Cross Linked Polyethylene) insulating material of 10 KV and below applicable to extrusion one-step method
  • Low-retraction silicane XLPE (Cross Linked Polyethylene) insulating material of 10 KV and below applicable to extrusion one-step method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The composition, ratio and model of the 10KV and below low-retraction silane XLPE insulating material suitable for the extrusion one-step method in this embodiment are shown in Table 1:

[0042] Table I

[0043]

[0044] In the present embodiment: the mechanical property, physical property, electrical property of its insulating material are shown in Table two:

[0045] Table II

[0046] serial number

[0047] serial number

Embodiment 2

[0049] The composition, ratio and model of the 10KV and below low-retraction silane XLPE insulating material suitable for the extrusion one-step method in this embodiment are shown in Table 3:

[0050] Table three

[0051]

[0052] In the present embodiment: the mechanical performance, physical performance, electrical performance of its insulating material are shown in Table 4:

[0053] Table four

[0054] serial number

[0055] serial number

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
tensile yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a low-retraction silicane XLPE (Cross Linked Polyethylene) insulating material of 10 KV and below applicable to an extrusion one-step method. The low-retraction silicane XLPEinsulating material comprises the following components in parts by weight: 100 parts of linear low-density polyethylene, 1-1.5 parts of silicane, 0.04-0.10 part of initiator, 0.05-0.15 part of antioxidant, 0.01-0.05 part of anti-copper agent, 0.02-0.15 part of catalyst and 0.10-0.50 part of lubricant. The insulating material produced according to the invention is applicable to the process that the silicane, the initiator, the catalyst and the like are directly added into a same extruder for granulation by the one-step method, so that the insulating shrinkage test performance of a silicane XLPE insulating cable of 10 KV and below is improved, and meanwhile, insulating shrinkage test of the silicane XLPE insulating cable of 10 KV and below produced by using an extrusion mold can extremely easily reach index requirements.

Description

technical field [0001] The invention relates to an XLPE insulating material for cables, in particular to a 10KV and lower low-retraction silane XLPE insulating material suitable for extrusion-type one-step production. Background technique [0002] Polyethylene is a high-quality chemical raw material. Through the cross-linking reaction, the polyethylene molecule changes from a two-dimensional structure to a three-dimensional network structure. The chemical and physical properties of the material are correspondingly enhanced, and the temperature and pressure resistance performance is improved. The material is cross-linked polyethylene, usually represented by its English abbreviation XLPE. [0003] The cross-linking methods of polyethylene include physical cross-linking, that is, radiation cross-linking and chemical cross-linking. Chemical crosslinking is divided into two types: silane crosslinking and peroxide crosslinking. [0004] At present, the production process of cros...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L51/06C08F255/02H01B3/44
Inventor 田维生
Owner FAR EAST CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com