Anti-skid sole and preparation method thereof

A kind of rubber and quality technology, applied in the field of shoe soles and anti-skid soles, can solve the problems of decreased anti-skid performance, fast sole wear, high anti-skid performance, etc. Effect

Active Publication Date: 2015-04-08
广州市邦尔福鞋材有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the prior art, some soles have good anti-skid performance under the condition of patterns at first, but the soles wear out quickly, and the anti-skid performance declines quickly
For ice skid performance and oil-water anti-skid performance, the existing technology cannot exert the expected high anti-skid performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A shoe sole of the present invention is made up of the following components by mass: 55 parts of nitrile rubber, 22 parts of bromobutyl rubber, 21 parts of butadiene rubber, 8 parts of natural rubber, 28 parts of nano silicon dioxide, glass fiber 22 parts, the length of which is 3mm, 3.5 parts of nylon fiber, 1.2 parts of PEG4000, 2.2 parts of white smoke active agent HC650, 1.6 parts of stearic acid ST / A, ZnCO 3 4.5 parts, 1.2 parts of antioxidant BHT, 2.2 parts of silane coupling agent, 5.5 parts of anti-slip agent, 0.5 parts of microcrystalline wax, 2.0 parts of sulfur, 2.5 parts of vulcanization accelerator TBBS.

Embodiment 2

[0018] Another kind of shoe sole of the present invention is made up of the following components by mass: 45 parts of nitrile rubber, 18 parts of bromobutyl rubber, 25 parts of butadiene rubber, 6 parts of natural rubber, 32 parts of nano silicon dioxide, glass 18 parts of fiber, the length of which is 4mm, 3.5 parts of nylon fiber, 1.2 parts of PEG-4000, 1.8 parts of white smoke active agent HC650, 1.4 parts of stearic acid ST / A, ZnCO 3 3.5 parts, 0.8 parts of antioxidant BHT, 2.2 parts of silane coupling agent, 5.5 parts of anti-slip agent, 0.5 parts of microcrystalline wax, 1.5 parts of sulfur, 2.0 parts of vulcanization accelerator TBBS.

Embodiment 3

[0020] Another kind of shoe sole of the present invention is made up of the following components by mass: 50 parts of nitrile rubber, 20 parts of bromobutyl rubber, 23 parts of butadiene rubber, 7 parts of natural rubber, 30 parts of nano silicon dioxide, glass 20 parts of fiber, 4 parts of nylon fiber with a length of 3.5 mm, 1 part of PEG4000, 2 parts of white smoke active agent HC650, 1.5 parts of stearic acid ST / A, ZnCO 3 4 parts, 1 part of antioxidant BHT, 2 parts of silane coupling agent, 5 parts of anti-slip agent, 0.5 parts of microcrystalline wax, 1.7 parts of sulfur, 2.5 parts of vulcanization accelerator TBBS.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
friction coefficientaaaaaaaaaa
friction coefficientaaaaaaaaaa
friction coefficientaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sole and a manufacturing method for the sole, and aims to provide a sole with high abrasion resistance and anti-skid property. According to the technical scheme, the sole consists of the following components in part by mass: 45 to 55 parts of nitrile rubber, 18 to 22 parts of brombutyl rubber, 21 to 25 parts of butadiene rubber, 6 to 8 parts of natural rubber, 28 to 32 parts of nano silicon dioxide, 18 to 22 parts of glass fiber, 3.5 to 4.5 parts of nylon fiber, 0.8 to 1.2 parts of polyethylene glycol 4000 (PEG 4000), 1.8 to 2.2 parts of rubber white smoke active agent, 1.4 to 1.6 parts of stearic acid, 3.5 to 4.5 parts of ZnCO3, 0.8 to 1.2 parts of antioxidant, 1.8 to 2.2 parts of coupling agent, 4.5 to 5.5 parts of anti-skid agent, 0.5 part of microcrystalline wax, 1.5 to 2.0 parts of sulfur, and 2.0 to 2.5 parts of vulcanization accelerator. The invention belongs to the technical field of making of shoes.

Description

technical field [0001] The invention relates to a shoe sole, specifically a non-slip shoe sole. The invention also discloses a manufacturing method of the shoe sole, which belongs to the technical field of shoe manufacturing. technical background [0002] The anti-slip property of the sole directly affects the comfort and safety of the shoe when it is worn. Many countries and regions have included the anti-slip property of soles as one of the mandatory inspection items for the production and quality inspection of imported and exported shoes. The improvement of the slip resistance of the sole can further improve the quality of the shoe. Guaranteeing the safety of consumers' wearing will help my country to break through the weight trade barriers of footwear importing countries, continue to maintain its status as a major footwear exporter, and win the reputation of a high-quality footwear exporter. [0003] my country is the world's largest manufacturing and exporting country...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L9/00
Inventor 景玉峰
Owner 广州市邦尔福鞋材有限公司