Production process of fabric

A production process and fabric technology, which is applied in the processing of textile materials, continuous processing of textile materials, and fabric surface trimming, etc., can solve the problems of impaired memory function of fabrics, high defect rate, and low production efficiency of looms. Unique memory function, soft feel, glossy effect

Inactive Publication Date: 2013-04-10
JIANGSU HUANGGUOSHU GARMENT
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This invention patent is suitable for the production process of high-crimp polyester low-stretch yarn with PTT performance. The PTT products produced have high defect rate, large loss of raw materials, low production efficiency of looms, improper process control, and easy to produce tension. Average, after willow blemishes, the dyeing and finishing treatment feels rough, and the memory function of the fabric is seriously damaged

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A production process of a fabric, comprising the following process steps:

[0019] 1) Warp the PTT silk in batches and wind it into a PTT silk pulp shaft. The warping speed is 185 m / min, and the hardness of the pulp shaft is 81%;

[0020] 2) The paddle shaft is stored in an air-conditioned cold room and shrinks for 46 hours;

[0021] 3) Pass the warped PTT wire through the size tank to soak the slurry, the slurry concentration is 11%, the temperature is 38°C, and the sizing rate is 4%; then it is dried in a drying room to make a PTT shaft coated with a size film, and the drying room temperature is 121°C, the PTT shaft hardness is 48%; the continuous processing speed of sizing and drying is 210 m / min, and the elongation of PTT wire is controlled at -0.6%;

[0022] 4) Put the PTT shaft on the warp beam frame of the doubling machine, use the staggered 3-reed rowing method, evenly arrange the PTT wires into the expansion reed, adjust the reed width, combine and wind into a...

Embodiment 2

[0030] A production process of a fabric, comprising the following process steps:

[0031] 1) Warp the PTT silk in batches and wind it into a PTT silk pulp shaft. The warping speed is 180 m / min, and the hardness of the pulp shaft is 78%;

[0032] 2) The paddle shaft is stored in an air-conditioned cold room and shrinks for 45 hours;

[0033] 3) Pass the warped PTT wire through the size tank to soak the slurry, the slurry concentration is 9%, the temperature is 35°C, and the sizing rate is 3%; then it is dried in a drying room to make a PTT shaft coated with a size film, and the drying room temperature is 115°C, the PTT shaft hardness is 45%; the continuous processing speed of sizing and drying is 200 m / min, and the elongation of PTT wire is controlled at -0.7%;

[0034] 4) Put the PTT shaft into the warp beam frame of the doubling machine, use the method of staggering 3 reeds to arrange the PTT wire evenly into the expansion reed, adjust the reed width, combine and wind it int...

Embodiment 3

[0042] A production process of a fabric, comprising the following process steps:

[0043] 1) Warp the PTT silk in batches and wind it into a PTT silk pulp shaft. The warping speed is 250 m / min, and the hardness of the pulp shaft is 83%;

[0044] 2) The paddle shaft is stored in an air-conditioned cold room and shrinks for 47 hours;

[0045] 3) Pass the warped PTT wire through the size tank to soak the slurry, the slurry concentration is 12%, the temperature is 40°C, and the sizing rate is 5%; then it is dried in a drying room to make a PTT shaft coated with a size film, and the drying room temperature is 125°C, the PTT shaft hardness is 55%; the continuous processing speed of sizing and drying is 220 m / min, and the elongation of PTT wire is controlled at -0.4%;

[0046] 4) Put the PTT shaft on the warp beam frame of the doubling machine, use the method of staggering 3 reeds to arrange the PTT wire evenly into the expansion reed, adjust the reed width, combine and wind it into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production process of fabric, and the production process comprises the following steps of (1) warping polytrimethylene terephthalate (PTT) yarns in batches; (2) scaling pulp axis; (3) padding PTT yarns into pulp, and drying the PTT yarns to be made into a PTT beam which is coated with pulp film; (4) installing the PTT beam into a warp rebeaming machine warp shaft frame to be coiled collectively into a warp beam; (5) dividing the warp beam into three strands on a lease machine; (6) sequentially penetrating PPT yarns on the warp beam into a harness wire and reeds according to a fabric drafting method and a reeding way; (7) weaving the yarns into fabric; (8) desizing the fabric; (9) dying the fabric; and (10) thermally setting the fabric to be made into the finished product fabric. Due to the adoption of the production process, the fabric has a unique memory function, a completely iron-free effect can be realized, softness in touching can be realized, the fabric is bright in color, and a wicking perspiration function and ultraviolet resistance function also can be realized.

Description

technical field [0001] The invention relates to a production process of a fabric, in particular to a production process of a memory fabric. Background technique [0002] Chinese patent CN101220536, a high-shrinkage polyester low-stretch yarn with PTT performance and its production process, using the orthogonal experimental statistical method to obtain a group or array of process parameters and related product data, from which the most reasonable process can be obtained Parameters and product performance indicators are continuously optimized on this basis to obtain process parameters and produce related products. This invention patent is suitable for the production process of high-crimp polyester low-stretch yarn with PTT performance. The PTT products produced have high defect rate, large loss of raw materials, low production efficiency of looms, improper process control, and easy to produce tension. All, after the willow defect, the dyeing and finishing treatment feels roug...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06B21/00D06C7/02D06B3/04D06B1/04D03D15/00D03D15/283
Inventor 王玉祥
Owner JIANGSU HUANGGUOSHU GARMENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com