Process for preparing rubber compound of ethylene propylene diene monomer waterproof roll

A technology of waterproof membrane and EPDM, which is applied in the field of compound rubber preparation technology of EPDM waterproof membrane, can solve the problems of high labor intensity and high energy consumption, and achieve the reduction of labor intensity, reduction of environmental pollution, The effect of stable product quality

Active Publication Date: 2013-05-01
常熟市三恒建材有限责任公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem mainly solved by the present invention is to provide the preparation process of mixed rubber for EPDM waterproofing membrane, which solves the disadvantages of high energy consumption and high labor intensity in the preparation process of mixed rubber for waterproofing membrane in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for preparing rubber compound of ethylene propylene diene monomer waterproof roll

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The preferred embodiments of the present invention will be described in detail below in conjunction with the accompanying drawings, so that the advantages and features of the present invention can be more easily understood by those skilled in the art, so as to define the protection scope of the present invention more clearly.

[0020] see figure 1 , the embodiment of the present invention provides the preparation process of the mixed rubber of EPDM waterproofing membrane, comprising the following steps:

[0021] a. Mixing, put the prepared raw materials into the internal mixing chamber of the internal mixer for internal mixing for 6 minutes, and discharge continuous rubber strips;

[0022] b. Filtering rubber, continuously add continuous rubber strips into the feeding port of the rubber filtering machine, and cut off the rubber strips with a thin steel wire when the length of the filtered rubber strips is 500-600mm;

[0023] c. To output the film, put the cut rubber st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a process for preparing a rubber compound of an ethylene propylene diene monomer waterproof roll. The process comprises the following steps: compounding, filtering rubber, yielding sheets, sulphurating and yielding strips. With the adoption of the manner, in the process for preparing rubber the compound of the ethylene propylene diene monomer waterproof roll, during sulphurating, an open mill is replaced with an internal mixer for sulphurating and compounding. A film cooling machine is used for guaranteeing timely and rapid cooling of the sulphurated rubber compound firstly in the industry, the quality of a prepared product is stable, linkage operation of the internal mixer, a rubber filter, a sheet-outputting machine and the film cooling machine, the energy consumption is reduced, the labor intensity of workers is reduced, the environmental pollution is reduced, and the production efficiency is improved.

Description

technical field [0001] The invention relates to the field of preparation technology of mixed rubber for waterproof coiled material, in particular to a preparation process for mixed rubber for EPDM waterproof coiled material. Background technique [0002] Waterproof membranes are used in roofs, storage tanks, dams, subways, railway and highway tunnels, and tank linings for agricultural irrigation. They are used in large quantities. In the past, asphalt felt was the main material, but now rubber and plastic membranes are the main materials. EPDM waterproofing membrane has become a high-grade membrane due to its excellent material properties. [0003] The rubber compound in the waterproof membrane is the raw material for manufacturing the coil, that is, the semi-finished product. Therefore, the colloidal dispersion quality of the rubber compound is directly related to the quality of the finished product. At the same time, the viscoelasticity and rheology of the rubber compound ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29B7/02B29B7/22C08L23/16
Inventor 吴建明潘叶明孙建民
Owner 常熟市三恒建材有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products