Methods for preparing and applying hot-dip galvanized screw thread protective agent

A technology of hot-dip galvanizing and protective agent, applied in hot-dip galvanizing process, coating, metal material coating process, etc., to achieve the effect of unaffected performance.

Active Publication Date: 2013-05-01
HULUDAO GUOLI IND FIRE ENVIRONMENTAL EQUIP MFG
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to overcome the defects of existing galvanized workpiece threaded buttons, the in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0008] Ingredients and pulping: In 1000 ml of xylene, add 50 grams of silicone resin, 35 grams of low-melting glass powder, 10 grams of chromium trioxide, 25 grams of china clay, and 15 grams of aluminum powder. After batching, it is stirred in a mixer at 1000-2000 rpm to form a protective agent slurry.

[0009] Coating method: After removing the rust and oil and dirt on the workpiece, place it in a temperature environment of 5 degrees Celsius, and use the protective agent slurry to coat the thread area of ​​the workpiece for 1-2 times, and control the thickness of the protective agent slurry to be 20-30 Between microns, place it at room temperature for more than 24 hours, so that the protective agent is dry and attached to the thread of the hot-dip galvanized workpiece, and then the workpiece is hot-dip galvanized.

[0010] Thread protection principle:

[0011] Since the protective agent slurry is composed of solvent, resin, metal oxide and glass powder, when it is coated on...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides methods for preparing and applying a hot-dip galvanized screw thread protective agent. The preparation method comprises the steps as follows: dosing and a preparing slurry: adding 50 grams of silicone resin, 35 grams of low melting point glass powder, 10 grams of chromium sesquioxide, 25 grams of china clay and 15 grams of aluminite powder, and stirring the mixture in a blender of 1000-2000 rpm after dosing, so that the protective agent slurry is formed. The applying method comprises the steps as follows: putting a workpiece under an environment at the temperature of 5 DEG C, coating screw thread areas of the wokpiece by the protective agent slurry, controlling the temperature of the protective agent slurry, and laying aside at the normal temperature, so that the protective agent is attached to the screw threads of the hot-dip galvanized workpiece in a dry state. The protective agent slurry can protect the screw threads against being pasted by zinc dross and an excessively thick zinc coating layer, so that defects are avoided, and the usage performance of the screw threads of a galvanized workpiece is not affected. The protective agent slurry can be applied to the methods for preparing and applying the protective agent of the screw threads of the hot-dip galvanized workpiece.

Description

technical field [0001] The invention provides preparation and application technology in the field of metal galvanizing, in particular a method for preparing and coating a hot-dip galvanized thread button protector. Background technique [0002] At present, when the protective agent is not used for the galvanized threaded thread of the workpiece, the threaded thread is stained with zinc material during hot-dip galvanizing, causing the threaded thread of the workpiece to be smeared by zinc slag and thicker zinc layer, and the size of the threaded thread becomes larger or changes. Small can not be connected with other thread fasteners. As a result, the hot-dip galvanized thread button end cannot be used normally, and even the entire workpiece is discarded, resulting in waste of the workpiece, and a waste of galvanized materials and working hours. Contents of the invention [0003] In order to overcome the defects of existing galvanized workpiece threaded buttons, the invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C2/04C23C2/02
Inventor 张建国吕志宏
Owner HULUDAO GUOLI IND FIRE ENVIRONMENTAL EQUIP MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap