Mono-component emulsion pressure-sensitive adhesive for surface protective film, and preparation method and application thereof

A surface protection film, single-component technology, applied in the direction of adhesive type, ester copolymer adhesive, etc., can solve the problems of pollution, increase production process, waste environment, etc., achieve good adhesion, eliminate glue mixing Effect of error, moderate peel strength

Active Publication Date: 2013-07-17
HUBEI INST OF AEROSPACE CHEMOTECH
View PDF4 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Adding an external cross-linking agent not only increases the production process, but also because the pot life of the emulsion pressure-sensitive adhesive after adding the cross-linking agent is usually less than 10 hours, the prepared unused pressure-sensitive adhesive and the residual pressure-sensitive adhesive in the glue tank not only cause waste and pollute the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The single-component emulsion pressure-sensitive adhesive for surface protection film of the present invention is prepared by polymerizing the raw materials of each component in a reactor, and its composition ratio is as follows in parts by weight:

[0041] Butyl acrylate 40.5

[0042] Vinyl acetate 2.2

[0043] Acrylic 0.9

[0044] N-methylolacrylamide 0.5

[0045] Allyl methacrylate 0.9

[0046] Sodium dodecyl diphenyl ether disulfonate 0.2

[0047] Ammonium persulfate 0.2

[0048] Sodium bicarbonate 0.1

[0049] Dimethylethanolamine 0.2

[0050] Deionized water 54.3.

[0051] The specific steps of the preparation method of the single-component emulsion pressure-sensitive adhesive for surface protection film of the present invention are as follows:

[0052] (1) Mix 60% deionized water, 75% ammonium persulfate, and all sodium dodecyl diphenyl ether disulfonate, butyl acrylate, vinyl acetate, acrylic acid, N-methylol acrylamide Add allyl methacrylate into the e...

Embodiment 2

[0057]The single-component emulsion pressure-sensitive adhesive for surface protection film of the present invention is prepared by polymerizing the raw materials of each component in a reactor, and its composition ratio is as follows in parts by weight:

[0058] Butyl acrylate 40.1

[0059] Vinyl acetate 1.8

[0060] Acrylic 1.8

[0061] N-methylolacrylamide 0.8

[0062] Allyl methacrylate 0.5

[0063] Sodium dodecyl diphenyl ether disulfonate 0.4

[0064] Ammonium persulfate 0.15

[0065] Sodium bicarbonate 0.2

[0066] 25% ammonia water 0.35

[0067] Deionized water 53.9

[0068] The specific steps of the preparation method of the single-component emulsion pressure-sensitive adhesive for surface protection film of the present invention are as follows:

[0069] (1) Mix 50% deionized water, 50% sodium dodecyl diphenyl ether disulfonate, 67% ammonium persulfate and all butyl acrylate, vinyl acetate, acrylic acid, N-methylol Add acrylamide and allyl methacrylate into t...

Embodiment 3

[0074] The single-component emulsion pressure-sensitive adhesive for surface protection film of the present invention is prepared by polymerizing the raw materials of each component in a reactor, and its composition ratio is as follows in parts by weight:

[0075] Butyl acrylate 38.3

[0076] Vinyl acetate 3.6

[0077] Acrylic 1.8

[0078] N-methylolacrylamide 0.8

[0079] Allyl methacrylate 0.5

[0080] Sodium dodecyl diphenyl ether disulfonate 0.3

[0081] Ammonium persulfate 0.1

[0082] Sodium bicarbonate 0.2

[0083] 25% ammonia water 0.4

[0084] Deionized water 54.0.

[0085] The specific steps of the preparation method of the single-component emulsion pressure-sensitive adhesive for surface protection film of the present invention are as follows:

[0086] (1) Mix 60% deionized water, 75% sodium dodecyl diphenyl ether disulfonate, 50% ammonium persulfate and all butyl acrylate, vinyl acetate, acrylic acid, N-methylol Add acrylamide and allyl methacrylate into t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Peel strengthaaaaaaaaaa
Peel strengthaaaaaaaaaa
Peel strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a mono-component emulsion pressure-sensitive adhesive for a surface protective film and a preparation method and application thereof. The mono-component emulsion pressure-sensitive adhesive for the surface protective film is a polyacrylate emulsion synthesized from butyl acrylate, vinyl acetate, acrylic acid, N-methylolacrylamide and allyl methacrylate by using a pre-emulsification semi-continuous polymerization process. The mono-component emulsion pressure-sensitive adhesive provided by the invention overcomes the disadvantage that a conventional pressure-sensitive adhesive for a protective film cannot be used without addition of a cross-linking agent; and the surface protective film prepared from the mono-component emulsion pressure-sensitive adhesive provided by the invention has moderate peeling strength and good adhesion on a PVC section bar, an alumina section bar and sheets of household electrical appliances, leaves no residual adhesive and spots after peeling and does not contaminate the PVC section bar, the alumina section bar and the sheets of household electrical appliances.

Description

technical field [0001] The invention relates to a single-component latex pressure-sensitive adhesive for surface protection film, and its application on the protective film of household appliances, the protective film of PVC profile and the protective film of aluminum oxide profile. Background technique [0002] With the rapid development of the national economy, building profiles and home appliances are used more and more widely in production and life. During the production, storage and transportation of PVC profiles and alumina profiles for construction and household appliances, the outer surface needs to be protected to prevent harmful gases, microbial corrosion, dust pollution, or avoid scratches caused by mechanical scratches, etc. . One of the most commonly used methods is now on the surface of the object to be protected, a layer of protective film (i.e. surface protective film) pasted, after finishing handling such as transportation, storage, processing and assemblin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/08C08F220/18C08F218/08C08F220/06
Inventor 冯小平李胜华姜云刚何伟武鹏
Owner HUBEI INST OF AEROSPACE CHEMOTECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap