Wearproof and high temperature resistant plastic pallet

A technology of plastic pallets and high temperature resistance, applied in the field of plastic pallets, can solve the problems of easy deformation, use restriction, plastic pallets are not resistant to high temperature, etc., and achieve the effect of low production cost and strong mechanical properties

Inactive Publication Date: 2013-07-24
青岛永卓真塑料制品有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, most of the plastic trays on the market are not resistant to high temperature. When the temperature exceeds 120°C, they are easily deformed. When the temperature is higher, they will volatilize toxic gases, so their use is subject to certain restrictions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A formula for wear-resistant and high-temperature-resistant plastic pallets. The raw materials are composed of the following ingredients in parts by weight: 100 parts of PE, 40 parts of PP, 30 parts of chitin, 15 parts of tourmaline crystal ore micropowder, 7 parts of organic silicon monomer, and 10- 15 parts, concentrated hydrochloric acid 1 part, acrylate 5 parts, guanidine hydrochloride 1 part.

[0013] The manufacturing process steps of a wear-resistant and high-temperature-resistant plastic tray are as follows:

[0014] (a) Melting and mixing 100 parts of PE, 40 parts of PP, 30 parts of chitin, and 15 parts of tourmaline crystal ore micropowder, and injection molding;

[0015] (b) First mix 7 parts of organosilicon monomer and 15 parts of ethanol, then mix with 1 part of concentrated hydrochloric acid, 5 parts of acrylate, and 1 part of guanidine hydrochloride, and stir for 20 minutes;

[0016] (c) Attach the mixture of (b) to (a), and the product is obtained afte...

Embodiment 2

[0018] A formula for wear-resistant and high-temperature-resistant plastic pallets. The raw materials are composed of the following ingredients in parts by weight: 100 parts of PE, 20 parts of PP, 15 parts of chitin, 10 parts of tourmaline crystal ore micropowder, 5 parts of organic silicon monomer, and 10 parts of ethanol , 0.5 parts of concentrated hydrochloric acid, 3 parts of acrylate, and 0.5 parts of guanidine hydrochloride.

[0019] The manufacturing process steps of a wear-resistant and high-temperature-resistant plastic tray are as follows:

[0020] (a) Melting and mixing 100 parts of PE, 20 parts of PP, 15 parts of chitin, and 10 parts of tourmaline crystal ore micropowder, and injection molding;

[0021] (b) First mix 5 parts of silicone monomer and 10 parts of ethanol, then mix with 0.5 parts of concentrated hydrochloric acid, 3 parts of acrylate, and 0.5 parts of guanidine hydrochloride, and stir for 20 minutes;

[0022] (c) Attach the mixture of (b) to (a), and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wearproof and high temperature resistant plastic pallet, which consists of the following components by weight: 100 parts of PE, 20-40 parts of PP, 15-30 parts of chitin, 10-15 parts of tourmaline crystal ore micropowder, 5-7 parts of an organosilicon monomer, 10-15 parts of ethanol, 0.5-1 part of concentrated hydrochloric acid, 3-5 parts of acrylate, and 0.5-1 part of guanidine hydrochloride. The plastic pallet provided in the invention is wearproof and high temperature resistant, and does not deform at 250DEG C.

Description

technical field [0001] The invention relates to a plastic pallet, in particular to a wear-resistant and high-temperature resistant plastic pallet. Background technique [0002] Most of the plastic trays currently on the market are not resistant to high temperatures. When the temperature exceeds 120°C, they are easily deformed. When the temperature is higher, they will volatilize toxic gases, so their use is subject to certain restrictions. Contents of the invention [0003] The object of the present invention is to provide a wear-resistant and high-temperature-resistant plastic tray to address the deficiencies of the prior art. [0004] In order to achieve the above object, the technical scheme adopted in the present invention is as follows: a formula for wear-resistant and high-temperature-resistant plastic trays, the raw materials are composed of the following parts by weight: 100 parts of PE, 20-40 parts of PP, 15-30 parts of chitin, electrical 10-15 parts of crystal o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/12C08L5/08C08K3/38C08J7/00
Inventor 李耀东
Owner 青岛永卓真塑料制品有限公司