Artware and fabrication method thereof

A production method and technology for handicrafts, applied in the field of handicrafts and their production, can solve the problems of low flexural and compressive strength of handicrafts, unenvironmental production process, and high production cost, and achieve environmental protection, low cost, and flexural and compressive strength of the production method. high effect

Inactive Publication Date: 2013-09-04
CHANGSHA INTAI BUILDING MATERIAL
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the prior art, the materials for making handicrafts are usually ceramics, gypsum materials or resin materials, plastics, etc., and the production process is relatively complicated. For example, the production of handicrafts with ceramic materials needs to be sintered at high temperature, and the production cost is high; the production process is not environmentally friendly; the handicrafts are resistant to bending Low compressive strength, such as plaster crafts; not resistant to low temperature, such as plastic crafts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1: Lion ornament and its production method

[0011] The lion ornament is composed of the following components by weight:

[0012] Magnesium Oxide 27%

[0013] Magnesium Chloride 13.5%

[0014] Vegetable fiber 10%

[0015] Filler 28%

[0016] Admixture 6%

[0017] Diffuser NNO 3%

[0018] Water 12.5%

[0019] The filler is one, two or three of quartz sand, vitrified microspheres and fly ash; the additive is one or two of chlorine partial emulsion and phosphate.

[0020] How to make lion ornaments:

[0021] (1) Dissolve magnesium chloride in water, then add the rest of the raw materials into the above solution, and stir in a mixer to form a slurry; (2) Pour the slurry into the mold, put the mold into a vacuum machine to discharge the air in the slurry ;(3) Take the mold out of the vacuum machine, place it for 3~5 hours, and demould after molding; (4) Place the handicraft after demoulding in a constant temperature and humidity box for 72 hours, and then ...

Embodiment 2

[0022] Embodiment 2: Roman column and manufacture method thereof

[0023] Roman columns are composed of component materials in the following weight ratios:

[0024] Magnesium Oxide 32%

[0025] Magnesium Chloride 15.5%

[0026] Vegetable fiber 10%

[0027] Filler 17%

[0028] Admixture 8%

[0029] Diffuser NNO 3%

[0030] Water 14.5%

[0031] The filler is one, two or three of quartz sand, vitrified microspheres and fly ash; the additive is one or two of chlorine partial emulsion and phosphate.

[0032] How to make a Roman column:

[0033] (1) Dissolve magnesium chloride in water, then add the rest of the raw materials into the above solution, and stir in a mixer to form a slurry; (2) Pour the slurry into the mold, put the mold into a vacuum machine to discharge the air in the slurry ;(3) Take the mold out of the vacuum machine, place it for 3~5 hours, and demould after molding; (4) Place the handicraft after demoulding in a constant temperature and humidity box for 72...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses artware which comprises the following raw materials in percentage by weight: 27-32% of magnesium oxide, 25-30% of magnesium chloride, 8-12% of plant fibers, 15-30% of packing, 6-8% of an additive, 2-4% of a diffusant NNO and the balance of water, wherein the packing is one, two or three of quartz sand, glass beads and fly ash; and the additive is one or two of polyvinylidene chloride latex and phosphate. The fabrication method comprises the steps of dissolving magnesium chloride in water, adding the rest raw materials in a solution, stirring uniformly in a stirrer to obtain slurry, pouring the slurry into a mold, then placing in a vacuum machine, exhausting air from the slurry, taking the mold out of the vacuum machine, placing for 3-5h, forming and demolding, placing the artware in a constant temperature humidity chamber for 72h, taking out the artware for natural drying, and trimming and coloring the artware. The artware is high in rupture strength and compressive strength, and resists low temperature, and the fabrication method is simple, environment-friendly and low in cost.

Description

technical field [0001] The invention relates to a handicraft and a manufacturing method thereof. Background technique [0002] In the prior art, the materials for making handicrafts are usually ceramics, gypsum materials or resin materials, plastics, etc., and the production process is relatively complicated. For example, the production of handicrafts made of ceramic materials needs to be sintered at high temperature, and the production cost is high; the production process is not environmentally friendly; handicrafts are resistant to bending Low compressive strength, such as plaster crafts; not resistant to low temperature, such as plastic crafts. Contents of the invention [0003] The object of the present invention is to provide a handicraft with high flexural and compressive strength, low temperature resistance, simple production method, environmental protection and low cost and its production method. [0004] In order to achieve the above object, the technical soluti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/32
Inventor 朱国家李世乾
Owner CHANGSHA INTAI BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com